Abstract
The effect of alkali metal salt on the activity of Co-Mo catalyst which has high resistance to sulfur poisoning for water gas shift reaction(WGSR) was studied. Two groups of catalysts were prepared to investigate the effects of anion and cation in alkali metal salts. For K-doped catalysts made with various potassium salts having different anion, the catalytic activity was explained to depend mainly on the BET surface area. Among the catalysts prepared by various nitrates of alkali metal as precursor, the Li-doped catalyst showed the best activity, and the others did not make significant differences giving relatively low activities. And the change of BET surface area by varying the loading of alkali metal showed a similar trend to that of activity. In this case, the activity was dependent on both BET surface area and the ratio of $Mo^{6+}$ with a tetrahedral coordination symmetry to $Mo^{6+}$ with an octahedral one, $Mo^6+[T]/Mo^{6+}[O]$ value.
황피독에 저항성을 가지는 수성가스 전환반응용 CoMo 계열 촉매에 알칼리금속염 첨가가 반응활성에 미치는 영향에 대하여 연구하였다. 알칼리금속염의 음이온과 양이온의 각각에 대한 영향을 알아보기 위하여 크게 두 경우로 나누어 촉매를 제조하였다. 그 하나는, 양이온을 K로 고정시키고 음이온을 변형시킨 경우로서, 반응활성의 변화는 BET 표면적의 변화로 설명되었다. 다른 한 경우는, 음이온을 $NO_3^-$로 고정시키고 알칼리금속 이온을 변형시킨 경우로서, Li가 첨가된 촉매의 활성이 가장 뛰어났으며 다른 양이온의 경우에는 서로 비슷한 낮은 활성을 보였다. 알칼리금속의 첨가량의 변화에 따른 BET 표면적의 변화와 반응활성의 변화가 같은 경향을 보였다. 알칼리금속염의 양이온을 변화시킨 경우에는 BET 표면적과 정8면체 배위구조 속의 $Mo^{6+}$에 대한 정4면체 배위구조 속의 $Mo^{6+}$의 비, 즉 $Mo^6+[T]/Mo^{6+}[O]$ 값의 복합적인 관계를 통해 반응활성의 변화를 설명할 수 있었다.