The Effect of Heat Treatment on Shrinkage and Mechanical Properties of PET Filament

섬유공정에서의 습.건열처리가 PET 필라멘트사의 열수축과 인장특성에 미치는 영향

This paper investigates the change of mechanical properties and thermal shrinkage in commercial multi-filament PET(polyethylene terephthalate) , namely, regular yarn, POY, DTY and composite yarn. To determine changing the effects of processing steps, these were examined at three steps process simulation conditions. The first step is sizing simulation$(S-1\;step\;:\;130^\circ{C}\times2\;min$., hot air treatment under 0.1 gf/d load), the second step is scouring simulation$(S-2\;step\;:\;100^\circ{C}\times20\;min$., boiling water treatment under free tension)and final step is setting simulation$(S-3\;step\;:\;180^\circ{C}\times2\;min$., hot air treatment under free tension). Regular yarn in multi-step treatment showed higher shrinkage at S-3 step and DTY showed higher in at S-1 step. While POY was relaxed at S-1 step, composite yarn showed different shrinkage properties depending on composite yarn type. Mechanical properties showed good relationship with shrinkage : high shrinkage makes initial modulus decrease and bleating strain increase. It also makes decreasing yield strain and yield stress decrease.