HIP처리한 초미립 WC-(5~20) mass% Co 초경 합금의 미세조직과 기계적 성질

Microstructures and Mechanical Properties of HIPed Submicron WC-(5~20) mass% Co Cemented Carbides

  • 이승원 (한양대학교 금속재료공학과) ;
  • 이완재 (한양대학교 금속재료공학과)
  • 발행 : 1998.12.01

초록

The microstructures and mechanical properties of submicron WC-Co cemented carbides were investigated in relation to cobalt content. To inhibit the WC grain growth during sintering, VC was added as a inhibitor in each alloy with 3 mass% to the cobalt content. The WC-(5, 8, 10, 15, 20) mass% Co compacts were sintered at $1400^{\circ}C$ for 30 min in vacuum. Some of WC-(5, 8, 10) mass% Co sintered compacts were HIPed with 120 atm at 130$0^{\circ}C$ for 1 hr. The shrinkages of all HIPed alloys were increased without depending on the cobalt contents and the sintered densities of them. The relative densities of the alloys were increased with the cobalt content and HIPing. The less the cobalt content, the larger the WC grain. Many contiguities of WC grains were found in WC-5 mass% Co alloy. The sizes and numbers of pores in the alloys were decreased by HIPing. And also the strength and the hardness of each alloy were increased. The maximum hardness was about 18.95 GPa in the WC-5 mass% Co alloy HIPed and the maximum transverse-rupture strength (T.R.S.) 3.2 GPa in the WC-20 mass% Co alloy sintered.

키워드

참고문헌

  1. Powder Met. v.31 N.Nordgren;A.Melander
  2. Refractory & Hard Mat. v.8 Chen Mian
  3. 粉體ぉよぴ粉末冶金 v.19 林;福家;鈴木
  4. 粉體ぉよぴ粉末冶金 v.32 鈴木;德木
  5. 粉體ぉよぴ粉末冶金 v.19 林;福家;鈴木
  6. Powder Met.Inter. v.16 M.Schreiner;T.Schmitt;E.Lassner;B.Lux
  7. Mat.Sci and Tech. v.7 S.K.Bhaumik;G.S.Upadhyaya;M.L.Vaidya
  8. 粉體ぉよぴ粉末冶金 v.27 鈴木;林
  9. Powder Metallurgy v.13 E.Larder
  10. 한국분말야금학회지 v.3 이승원;이완재
  11. PM'94 Powder Metallirgy World Congress v.1 B.K.Kim;G.H.Ha;J.H.Lee;W.J.Lee
  12. J.Matals v.5 R.I.Fullman
  13. 粉體ぉよぴ粉末冶金 v.19 林;福家;鈴木