Abstract
The purpose of this study was performed to compare to the characteristics (microstructure, phase change and hardness, erosion rate) of HVOF sprayed coatings with 20wt% NiCr claded and 7wt%NiCr mixed $\textrm{Cr}_{3}\textrm{C}_{2}$ powder. In the case of the 20wt% NiCr claded $\textrm{Cr}_{3}\textrm{C}_{2}$ powder, microstructural feature showed that the primary $\textrm{Cr}_{3}\textrm{C}_{2}$ was remained in the coating but was barely remained in the mixed $\textrm{Cr}_{3}\textrm{C}_{2}$ coating. As a results of XRD analysis, both 20wt%NiCr claded and 7wt% NiCr mixed $\textrm{Cr}_{3}\textrm{C}_{2}$ powder was decomposed during spraying but the degree of decomposition of the 20wt%NiCr claded was lower than 7wt%NiCr mixed $\textrm{Cr}_{3}\textrm{C}_{2}$ powder. After spraying the mixed powder for microhardness was higher than claded $\textrm{Cr}_{3}\textrm{C}_{2}$ powder and which was increased up to $\textrm{Hv}_{300}$= 1665 after heat treatment to $1000^{\circ}C$. however. 20wt%NiCr claded $\textrm{Cr}_{3}\textrm{C}_{2}$ became to decrease at $600^{\circ}C$ which was the maximum.
20wt%NiCr이 크래드된 크롬카바이드 분말과 7wt%NiCr이 기계적으로 혼합된 크롬카바이드 분말을 이용하여 HVOF 용사된 용사층의 특성(미세조직, 결정상, 경도값 그리고 erosion rate)을 비교하였다. 용사상태의 미세조직강의 특성은 크래드분말의 경우에 primary $\textrm{Cr}_{3}\textrm{C}_{2}$상이 용사층에는 남아 있었으나 혼합분말의 경우에는 primary $\textrm{Cr}_{3}\textrm{C}_{2}$ 상은 용사층에 거의존재하지 않았다. 또한 XRD 분석결과 두 분말 모두 용사과정에서 크롬카바이드의 분해는 일어났으나 분해율은 크래드분말의 경우가 혼합분말보다 낮았다. 용사상태에서 경도값은 혼합분말의 경우가 높았으며 $1000^{\circ}C$까지 열처리 후 혼합분말의 경도값은 1665까지 증가하였으나 크래드분말은 $600^{\circ}C$를 정점으로 감소하는 경향을 보였다.