Fracture Toughness of IC Molding Compound Materials(II)

IC 몰딩 콤파운드 재료의 파괴 인성치(II)

  • Published : 1998.05.01

Abstract

Cracking problem of Epoxy Molding Compound(EMC) is critical for the reliability of the plastic package during temperature cycling and IR-reflow condition. Fracture toughness of EMC, which is defined as the resistance of EMC to the crack propagation, is a useful factor in ht estimation of EMC against package crack. Thus, development of EMC having high fracture toughness at a given loading condition would be important for confirming the integrity of package. In this study, toughness of several EMC was measured by varying the test conditions such as temperature, loading speeds, and weight percent of filler in order to quantify the variation of toughness of EMC under various applicable conditions. It was found from the experiments that toughness of all EMC has following trends, i.e., it rapidly decreases over the glass transition temperature, remains almost same or little decreases below $0^{\circ}C$. It decreases with the growth of cross head speed in EMC and the weight percent of filler as the degree of brittleness of EMC increases with the amount of filler content.

Keywords

References

  1. Polymer Engineering and Science v.30 Theermomechanical Properties of IC Molding Compounds H.E.Bair;D.J.Boyle
  2. 日本機械學會論文集 v.56 no.510 A Study of Package Cracking during the Reflow Soldering Process Makoto Kitano;Sueo Kawai;Asao Nishimura;Kunihiko Nishi
  3. 전기전자재료학회지 반도체 봉지수지의 파괴 인성치 측정 및 패키지 적용 김경섭;신영의
  4. Polymer Testing 8 no.8 On the Determination of Fracture toughness in Polymers Kim, B. H.;Joe, C. R.;Otterson, D. M.
  5. 파괴역학(이론·해석에서 공학적 응용까지) 장동인;정경섭
  6. American Chemical Society Rubber Toughened Plastics C. Keith Riew