시트르산의 양과 소결온도에 따른 (La,Sr)$MnO_3/Gd_{0.2}Ce_{0.8}O_{1.9}$ 계면특성

Characterization of (La,Sr))$MnO_3/Gd_{0.2}Ce_{0.8}O_{1.9}$ Interface with Citric Acid Contents and Sintering Temperature

  • 윤일영 (고려대학교 공대 재료공학과) ;
  • 윤희성 (고려대학교 공대 재료공학과) ;
  • 김병호 (고려대학교 공대 재료공학과)
  • 발행 : 1998.01.01

초록

G $d_{0.2}$C $e_{0.8}$ $O_{1.9}$(CGO) for electrolyte and L $a_{0.5}$S $r_{0.5}$Mn $O_3$(LSM50) for cathode in Solid Oxide Fuel Cells(SOFC) were synthesized by citrate process. Specimens were prepared with sintering temperatures at 110$0^{\circ}C$, 120$0^{\circ}C$ and 130$0^{\circ}C$, which were fabricated by slurry coating with citric acid contents. Interfacial resistance was measured between cathode and electrolyte using AC-impedance analyzer. With various citric acid content, the degree of agglomeration for the initial particles changed. Also sintering temperature changed the particle size and the degree of densification of cathode. Factors affecting the interfacial resistance were adherent degree of the electrolyte and cathode, distribution of TPB(three phase boundaries, TPB i.e., electrolyte/electrode/gas phase area) and porosity of cathode. By increasing the sintering temperature, particle size and densification of the cathode were increased. And then, TPB area which occurs catalytic reaction was reduced and so interfacial resistance was increased.sed.sed.d.

키워드

참고문헌

  1. Z. Electrochem. v.6 Uber die elecktrolytische Leitung fester korper bei sehr hohen Temperaturen W. Nernst
  2. Wiss. Verooff. Siemens Werken no.14 Uber stromlieferende Prozess im Konzentrationsgefalle fester Elektrolyte W. Schottky
  3. Characterisation of porous cathodes for application in solid oxides fuel cells Fred van Heuveln
  4. J. Electrochem. Soc. v.123 no.3 Mixed Electricai Conduction in the Flourite-type Ce$Ce{1_x}Gd_-xO_xO_{2_-x/2}$ T. Kudo;H. Obayashi
  5. J. Electrochem. Soc. v.16 no.9 C. S. Tedmon, Jr.;H. S. Spacil
  6. Method of Preparaing Lead and Alkaline Earth Titanates and Niobiates and Coating Method Using the Same to Form a Capacitor M. Pechini
  7. Characterisation of porous cathodes for application in solid oxides fuel cells Fred van Heuveln
  8. Am. Ceram. Bull v.68 no.5 Mixed-Cation Oxide Powders via Polymeric Precursors P. Lessing
  9. Solid State Ionics no.66 Electrical conductivity in Lal-xSrxMnO₃+δ J. A. M. van Roosmalen ;J. P. P. Huijsmans;L. Plom
  10. Chem. Letters Preparation of Perovskite-type Oxides with Large Surface Area by Cirtrate Process H. M. Zhang;Y. Teraoka;N. Yamazoe