Effect of Si on the Corrosion Properties of Mg-Li-Al Light Alloy

경량화 Mg-Li-Al합금의 내식성에 미치는 Si의 영향

Effect of Si in the electrochemical corrosion characteristics of Mg-Li-Al light alloy has been investigated by means of potentiodynamic polarization study. The elecrochemical behaviors were evaluated in 003% NaCl solution and the solution buffered with KH$_{2}PO_{5}{\cdot}$NaOH at room temperature. It was found that the addition of very small quantity of Si (0.48 wt%) in Mg-Li-Al light alloy increased corrosion rates and amount of corrosion products and decreated the pitting resistance of the alloy. From the results it was concluded that Si which is added to increase the strength of Mg-Li-Al alloy is harmful to corrosion properties of the alloy.

현재 구조용 합금으로는 최경량화인 Mg-Li-Al합금의 내식성에 미치는 Si의 영향을 전기화학적 분극시험에 의하여 조사하였다. 전기화학적 분극시험은 ${KH}_{2}{PO}_{5}$·NaOH 완충용액으로 pH7로 고정한 0.03% NaCl 전해액에서 Mg-Li-Al(A4)합금과 Mg-Li-Al에 Si을 0.48 wt% 첨가한 (S5)합금에 대하여 전류밀도에 따른 전위의 변화를 측정하였다. 실험 결과 미량의 Si를 첨가한 Mg-Li-Al-Si 합금의 경우가 Si을 첨가하지 않은 Mg-Li-Al 합금의 경우보다 부식속도가 증가하였으며, 부식생성물의 분포범위도 넓었고 생성량도 많았다. 이러한 실험결과를 고려해 볼 때, Mg-Li-Al 합금에 미량이지만 Sidl 첨가됨으로써 Mg-Li-Al 합금의 내식성이 감소된다고 판단된다. 따라서 강도특성이 향상을 목적으로 첨가하는 Si의 첨가량에 대해서는 적절한 양의 조정이 필요하다.