Abstract
We smelted thc pellets made by mixing the distilled carbon from wlISte Lires, LD converter dust and slag with reduction process in the revcrberatory furnace. Thc obtained results are as follows 1) The removal mte of zinc appears above 97% after T reducing the pellets at $1300^{\circ}C$ for Ihr and the zinc content in the residue are 0.1~D.2%. 2) Under the mixing condition of 500 g LD dust. 150-200 g LD slag and 30-50 g distilled carbon of waste lires the removal raho of zinc shows above 95%, while t the 50-60% Fe remains in the residue. 3) After smelting at $1350^{\circ}C$ for 3hrs, the recovery ratio of pig iron reduced from lhe p pellets containing 15-20% LD slag and 4.1-7.2% distilled carbon of waste tires appears in the range of 89.3-92%. 4) Tbe c chemical composition of the recovered pig iron is 1.7%C, O.05%P, 0.05%S and balance Fe. 5) Tbe recovered dust from the d dust collcctor alter finishing the reduction rcaction appears as a crude zinc oxide conLaining 60% zinc.
LD 제강 더스트를 제철원료로 LD 전로 제강 슬래그를 용제로 하고 폐타이어에 의해 제조한 건류탄을 환원제로 사용하여 반사로에서 환원 실험하여 배합비, 온도 및 반응시간 변화에 따른 환원율 및 철 회수율의 영향을 조사하여 다음과 같은 결과를 얻을 수 있었다. 1) $1300^{\circ}C$에서 1시간 동안 환원실험한 결과 탈아연율(removal rate of zinc)이 97%이상이며 잔사중의 Zn은 0.1~0.2%이었다. 2)페렛트 중에 LD 스래그 15~20%, 폐타이어 건류탄 4.1~6.7% 함유된 시료를 대기압, $1350^{\circ}C$에서 3시간동안 환원실험한 결과 선철의 회수율은 89.3~92%이었다. 3)환원제련시에 집진장치에서 회수한 더스튼 Zn 60%의 조산화아연이었다. 4) 회수한 선철의 성분은 Fe 96%, C 1.6%, P 0.08%, S 0.05%이었다. 5) 환원시에 생성한 슬래그의 조성은 $Ca_2Al_2SiO_7$, 8CaO $5SiO_2$ 및 $Na_3Ca_6(PO_4)_5$가 확인되었다.