Effect of Plastic Injection on the Blast Furnace Operation Under One-Tuyere Test

플라스틱의 풍구 1본 시험흡입에 따른 고로조업영향

Recently, the new technology for the recycling of waste plastics as an alternative he1 of blast furnace ha been developed. In this shldy, the test of plastics injection into a tuyere af the foundry blast furnace were carried out. The injection rate of plastics far this tcst facility war expressed as follows, ${W}_{s}=0.265\frac{{delta}PA}{U}_{g}$, where. Ws, AP, A and Ug are plastic conveying ratc (kgisec), pressure drop between feed hopper and blaqt pressure (alm), cross sectional area of conveying pipe (mi) and superficial velocity of transport air (mhzc) respcctiuely. From the results of semi-continuous test operation during 96 hours, the replacement raho mned out to be 1.38 according to the injection rate of 6. 4 kg-plasticsit-p. With increasing the rate of plaslics injcchon, the content of hydrogen in top gas became increased and the brick temperahlre at bzlly was also increased due to Lhe changes ot the combustion zone shape.

최근 선진국에서는 폐플라스틱을 고로의 대체연료로 이용하려는 기술개발이 시도되고 있다. 본 연구에서는 포항제철 주물선 고로 풍구 1본을 대상으로 시험취입을 실시한 결과, 플라스틱의 취입속도는 다음과 같이 나타낼수 있었다. ${W}_{s}=0.265\frac{{delta}PA}{U}_{g}$ 여기서 Ws, ΔP, A 그리고 Ug는 각각 플라스틱 수송속도(kg/sec), 공급용기내의 압력과 송풍압력의 차이(atm), 수송배관의 단면적($m^2$) 그리고 총 수송공기 유속(m/sec)이다. 약 96시간의 조업기간중 최대 취입비 6.4kg-plastic/t-p까지의 반연속 시험취입 조업결과, 치환율은 1.38정도였다. 플라스틱이 취입됨에 따라 노정가스중 수소의 함량은 증가하였으며, 연소대 형상변화에 따라 bellyqn 노체의 온도는 상승하였다.