Abstract
In relation to the application of magnetic method to the evaluation of irradiation damage (embrittlement) changes in the magnetic parameters(hysteresis loop and Barkhausen noise) and Vickers microhardness due to neutron irradiation and heat treatment were measured and compared. In the case of irradiation $(2.3{\times}10^{19}\;n/cm^2,\; E{\ge}1\;Mev,\; 288{\circ}C)$ hysteresis loop measurements show that susceptibility decreases as coercivity increase. Saturation magnetization do not show any change. Barkhausen noise amplitude and Barkhausen noise energy have decreased while Vickers microhardness has increased. For isothermally heat treated condition of irradiated specimen at 470 $^{\circ}C$ and 540 $^{\circ}C$, Barkhausen noise energy has increased while Vickers microhardness has decreased. Results of BNE and Vickers microhardness are reversed to the results on irradiated condition. All these consistent changes in magnetic parameter and Vickers microhardness measurement, which are thought to be resulted from the interaction between irradiation-induced defects and dislocation, and magnetic domain, respectively, show a possibility that magnetic measurement may be used to the evaluation of material degradation and recovery due to neutron irradiation and heat treatment, respectively, if a relevant large database in prepared.
자기측정법에 의한 조사손상 평가 가능성을 조사하기 위하여 SA508 CI.3강 모재금속의 중성자 조사 및 열처리 온도에 따른 자기특성(자기이력곡선, Barkhausen Noise(BN) 진폭, BN 에너지)과 경도 변화를 측정 비교하였다. 중성자 조사에 따라 자화율, BN 진폭, BN 에너지는 감소하였고 보자력과 경도는 증가하였으며, 포화자화 값은 변화하지 않았다. 열처리된 조사시편의 경우, 열처리 온도 증가에 따라 BN 에너지는 증가하였으며, 경도는 감소하였다. 결함과 전위혹은 자벽 이동과의 상호작용에 의한 경도 및 자기특성의 일관성 있는 변화는 원자로 압력용기 재료의 조사손상 평가와 관련 자기적 측정법 응용 가능성을 보여주었다.