Abstract
$Nd_{15}Fe_{77}B_8$ and $Nd_{16}Fe_{76}B_8$ powders were prepared by mechanical alloying in Ar atmosphere, and their phases and magnetic properties were investigated with as a function of the annealing temperature. It was found that the mechanical alloyed $Nd_{16}Fe_{76}B_8$ powder for 450 hours was amorphous phase with a part of $\alpha$-Fe crystallites. The obtained powders at 700 $^{\circ}C$ for 30 minute resulted in two phase of $Nd_2Fe_{14}B$ and $NdB_6$ by the solid-state reaction. The mechanical alloyed $Nd_{16}Fe_{76}B_8$ powder for 450 hour and annealed at 700 $^{\circ}C$ for 30 minute was showed $_iH_c\;of\;9.91\;kOe,\; B_{max}\;of\;12.93\;kG,\;Br\;of\;7.6\;kG\;and\;(BH)_{max}\;10.1\;MGOe$.
Ball Mill을 이요하여 Ar 분위기에서 기계적합금법으로 Nd15Fe77B8과 Nd16Fe76B8 분말을 제조하고, 제조된 분말을 연속 진공열처리 시킨 후 열처리온도에 따른 상변화 및 자기적 성질을 조사하엿다. 450시간 볼밀도처리한 Nd15Fe77B8과 Nd16Fe76B8 합금 분말에서 Nd와 B의 피크는 보이지 않고 전체적으로 $\alpha$-Fe 결정상만 존재하고 있었으며, 이를 $700^{\circ}C$에서 30분간 열처리를 시키면 고상반응에 의하여 Nd2Fe14B와 소량의 NdB6이 흔재된 상을 얻을 수 있었다. $700^{\circ}C$로 열처리 한 Nd16Fe76B8 합금 분말은 iHc9.9kOe, Bs, 12.9 KG, (BH)max 10.1 MGOe의 자기적 성질을 나타내었다.