Grafting of Performed Polyacrylonitrile onto Cellulose Acetate

Polyacrylonitrile과 셀룰로오스 아세테이트의 그라프팅에 관한 연구

The cellulose modification can be made in steps, giving a range of new products having properties quite different from the parent cellulose. Effective molecular weight control and narrow molecular weight distribution of the polyacrylonitrile can be accomplished by anionic polymerization technique. Preformed polyacrylonitrile was grafted precisely onto cellulose acetate by SN$_2$ reaction mechanism in a simple and effective way under homogeneous reaction condition. The 3.5g of completely dried cellulose acetate(DS=2.4) dissolved in 50ml of dry THF was transferred to the 215m1 polyacrylonitrile solution. The mixture was stirred vigorously under nitrogen atmosphere for 2 hrs. FTIR spectra of cellulose acetate and grafted cellulose acetate were taken, and their characteristic bands were identified.

자유라디칼 반응기구에 의한 그라프팅 반응은 셀룰로오스의 낮은 반응 참여율, 반응의 저조한 반복성, 반응조절의 난이점, 특히 homopolymer의 높은 발생율로 인한 그라프팅 반응의 낮은 치환도 등의 문제를 지니고 있다. 이러한 문제를 해결하기 위하여 음이온중합 방법으로 polyacrylonitrile을 조제한 후 셀룰로오스 아세테이트와 균일계 반응조건에서 이분차 친핵치환(SN2) 반응기구에 의하여 그라프트 공증합 반응을 실시하였으며, 시간의 변화에 다른 겔의 형성과 그라프트 공중합 반응 전 후의 셀룰로오스 아세테이트의 FTIR spectra의 중요한 흡수대를 비교하여 반응을 확인하였다.