초록
In this paper the Hardness and Electro-chemical corrosion of the Nimonic 80A superalloy were studied. It aging heat treatments was carried out at $650^{\circ}C$, $700^{\circ}C$, $750^{\circ}C$,$800^{\circ}C$ and $850^{\circ}C$ with different time of 20min , 30min 1hour, 2hours, 4hours, and 16hours additionally 64hours and 128hours at $650^{\circ}C$. The obtained results were as follows; 1. As aging temperature increased the time for the maximum hardness was reduced from 128hours at $650^{\circ}C$ to 30min at $850^{\circ}C$ whereas the highest hardness was reduced from Hv 381 at $650^{\circ}C$ to Hv 321 at $850^{\circ}C$. 2. In the Electro-chemical corrosion test as a function of aging heat treatment time and tem-perature the corrosion potential was reversely proportional to Hardness which indicated the effects of ${\gamma}/{\gamma}'$ coherency of base material and precipitate. 3. Initiation point of the pitting was observed at grain boundary twin boundary and near${\gamma}'$ pre-cipitates. The results of composition analysis by EDS at this point indicated that sulphur originat-ed from 1N $H_2SO_4$ solution was found in depletion at the grain boundaries and the pit which arouse in the near precipitates were lack of Al Ti and Ni which are the main element of ${\gamma}'$ The depletion of such element was cause breakdown of passive film.