Abstract
Fly ashes mixed with clay as 70:30 weight percent were sintered by microwave energy and a 2.45 Ghz kitchen model microwave oven was used. Samples were sintered at $1,150^{\circ}C$ and kept at that temperature up to 50 minutes by 10 minutes intervals. Microstructures were taken by Scanning Electron Microscope (SEM) and Energy Dispersive Spectrometry (EDS) analysis of a raw fly ash was taken. X-ray diffraction analysis was done, and compressive strengths and apparent densities were measured. Pore sizes of the samples became smaller as time passed by, but compressive strengths and apparent densities did not change much. Numerical analysis on the microwave heated system was carried out in order to figure out heat transfer phenomena in the cavity.
석탄회의 점노를 70:30의 비율로 혼합하여 마이크로파를 이용하여 소결하였으며, 소결에는 2.45Ghz의 일반가정용 마이크로파 오븐을 사용하였다. 시편은 $1,150^{\circ}C$에서 50분까지 10분 간격으로 소결하였다. 석탄회의 미세구조는 주사전자현미경(SEM)과 Energy dispersive spectrometry(EDS)를 이용하여 분석을 하였으며 X선회절 분석과 압축강도와 겉보기 비중을 추정하여 비교하였으며 시간이 지날수록 시편의 기공크기는 작아졌으나 압축강도와 겉보기 비중은 변화의 크기가 작았다. 로안에서의 마이크로파에 의한 시편으로의 열전달현상을 알아보기 위하여 컴퓨터를 이용한 수치해석을 행하였다.