Microstructural evolution in liquid-phase sintered $\alpha$-silicon carbide

액상소결 $\alpha$형 탄화규소의 미세구조 변화

  • Published : 1998.04.01

Abstract

After the addition of yttrium aluminum garnet of 2, 5, 10 mol% as a sintering aid, $\alpha$-silicon carbides were prepared by a liquid-phase sintering at $1850^{\circ}C$, and the microstructural evolution was investigated during sintering as functions of liquid-phase amount and sintering time. The highest apparent density in each compositions was obtained in specimens sintered for 2 h, and the percentage of weight loss increased with sintering time. By increasing the amount of sintering aid (yttrium aluminum garnet), the rate of grain growth during sintering decreased, but the apparent density of sintered body increased. The phase transformation from 6H-SiC to 4H-SiC was partially observed in specimens sintered for a long time, and so, a few rod-like grains were observed.

2, 5, 10 mol% YAG(yttrium aluminum garnet) 분말을 액상 소결조제로 $\alpha$상 탄화규소 분말에 첨가한 후 $1850^{\circ}C$에서 소결시간을 달리하여 소결체를 제조한 다음, 소결시 일어나는 미세구조 변화를 첨가된 액상량과 소결시간의 변화에 대하여 고찰하였다. 각 조성중 2시간 소결한 시편에서 가장 높은 밀도를 나타냈으며, 소결시간이 길수록 액상의 기화로 인하여 중량감소량이 점차 증가하였다. 또한 첨가된 YAG 액상량이 증가할 수록 상대밀도(apparent density)와 중량감소량은 증가하였으나 입성장속도는 감소하였다. 액상량이 적은 시편에서는 소결시간이 길수록 일부 6H상의 탄화규소 입자가 4H상 탄화규소 입자로 상전이 되었으며, 이로 인하여 막대상 입자들이 일부 존재하였다.

Keywords

References

  1. Structural Ceramics M. Srinivasan;J.B. Wachtmann. Jr(ed.)
  2. Silicon-Carbide Ceramics H. Tanaka;S. Somiya(ed.);Y. Inomata(ed.)
  3. Powder Metallurgy International v.21 K. Hunold
  4. Powder Metallurgy International v.10 no.2 W. Bocker;H. Hausner
  5. J. Am. Ceram. Soc. v.68 no.9 D.H. Stutz;S. Prochazka;J. Lorenz
  6. J. Mater. Sci. v.23 R.H.J. Hannink;Y. Bando;H. Tanaka;Y. Inomata
  7. J. Am. Ceram. Soc. v.65 no.6 M. Omori;H. Takei
  8. Am. Ceram. Soc. Bull. v.70 no.3 M.A. Mulla;V.D. Krstic
  9. J. Am. Ceram. Soc. v.77 no.2 N.P. Padture
  10. J. Am. Ceram. Soc. v.70 no.10 F.J. Klug;S. Prochazka;R.H. Doremus
  11. J. Mater. Sci. v.29 S.K. Lee;Y.C. Kim;C.H. Kim
  12. J. Am. Ceram. Soc. v.77 no.6 S.K. Lee;C.H. Kim
  13. J. Am. Ceram. Soc. v.76 no.3 L.S. Sigl;H.J. Kleebe
  14. J. Mater. Sci. v.23 M. Omori;H. Takei
  15. MRS Bull. v.20 V.D. Kristic
  16. J. Am. Ceram. Soc. v.71 no.4 T.R. Dinger;R.S. Rai;G. Thomas
  17. Mater. Lett. v.29 J.K. Lee;H. Tanaka;H. Kim;D.J. Kim
  18. J. Mater. Sci. v.29 M.A. Mulla;V.D. Krstic
  19. Ceramics Japan v.31 H. Tanaka