A Study on the Prediction of Fatigue Crack Growth Rate in Stainless Steel Weldments

스테인레스강 용접부의 피로균열 전파속도 예측에 관한 연구

  • Published : 1998.06.01
Download PDF
⟨ Previous Next ⟩

Abstract

Welding structure contains residual stress due to thermal-plastic strain during welding process, and its magnitude and distribution depend on welding conditions. Cracks initiate from various defects of the weldment, propagate and lead to final fracture, The crack initiation and propagation processes are affected by the magnitude and distribution. Therefore, the magnitude and distribution of weldment residual stress should be considered for safety design and service of welding structures. Also it is very important that more accurate assessment method of fatigue crack growth must take into account the redistributing the residual stress quantitively. because the residual stress in weldment has characteristics of its redistribution with loading magnitude, number of cycles and fatigue crack propagation. In this study fatigue crack behavior of STS-304 weldment was investigated during crack propagation into tensile residual stress region or compressive residual stress region. Crack growth rates were predicted and compared with experimental results.

Keywords

References

  1. Analysis of Welded Structure Masubuchi, K.
  2. Residual Stress Effects in Fatigue. ASTM STP 776 Influence of Residual Stress on the Predicted Fatigue Life of Weldments. Lawrence. F. V. Jr.;Burk. J. D.;Yung. J. Y.
  3. 대한용접학회지 v.5 no.1 용접잔류응력 영역에서의 피로균열전파에 대한 Forman식의 적용 이용복;김상철
  4. 대한기계학회 춘계학술대회논문집( I ) 잔류응력의 재분포와 피로크랙 전파거동 송삼홍;김현
  5. Japan Welding Society Transactions v.4 no.3 Redistribution of Residual Stress Caused by Crack Propagation Initially Through Residual Compressive Stress Field Mukai, Y.;Nishimura, A.;Kim, E.J.
  6. 대한용접학회지 v.13 no.4 피로균열이 진전할 때 용접잔류응력의 재분포와 그 영향 이용복;조남익
  7. 한국공작기계기술학회지 v.6 no.2 SS330 용접재에서 재분포 압축잔류응력 및 균열닫힘의 영향을 고려한 피로거동에 관한 연구 이용복;정진성;김호경;조남익;박상흡
  8. Engineering Fracture mechanics v.8 Analysis of the Stress Intensity Factor of a Crack Perpendicular to the Welding Bead Terada, H.
  9. Transactions of American Society for Steel Treating v.18 Green, O. V.
  10. The Stress Analysis of Cracks Handbook Tada, H.;Paris, P. C.;Irwin, G. R.
  11. Trans. ASME. J. Basic Eng. v.89 Numerical Analysis of Crack Propagation in Cyclic Loaded Structures Forman, R. G.;Kearney, V. E.;Engle, R. M.
  12. Damage Tolerance in Aircraft Structure, ASTM STP486 The Significance of Fatigue Crack Closure Elber. W.
  13. Japan Welding Society Transactions v.4 no.1 Redistribution of Residual Stress Caused by Crack Propagation Initially Through Residual Tensile Stress Field Mukai, Y.;Nishimura, A;Kim, E.J.
  14. 대한기계학회논문집(A) v.20 no.7 SS330용접재에서 재분포 잔류응력 및 균열닫힘영향을 고려한 피로거동에 관한 재분포에 관한 연구 이용복;정진성;조남익
  15. 대한기계학회 추계학술대회논문집(A) 연강용접재의 피로거동에 관한 연구 이용복;조남익;김호경;정진성;김영훈
  16. Scripta Metallurgica v.18 On the Development of Crack Closure with Crack Advance in a Ferrictic Steel Minakawa, K.;Nakamura, H.;Mevily, A.J.
  17. Journal of Engineering and Materials Technology. Trans. ASME H. v.102 Near-Threshold Fatigue Crack Growth in 2-1/2 Cr-Mo Pressure Vessel steel in Air and Hydrogen Ritchie, R.O.;Suresh, S.;Moss, C.M.
  18. Metallurgical Trans. A v.13 A Geometric Model for Fatigue Crack Closure Induced by Fracture Surface Roughness Suresh, S.;Ritchie, R.O.
  19. Int. J. of Fracture v.11 Crack Closure in Fatigue of a Titanium Alloy Bachmann, V.;Munz, D.
  20. J. of Basic Eng. Trans. of ASME A Critical Analysis of Crack Propagation Law Paris, P.;Erdogan
  21. ASTM STP 462 Effect of Environments and Complex Load History on Fatigue Life Walker, E. K.
  22. Fatigue of Eng. Materials & Structures v.14 no.4 Crack Closure and Plastic Zone Sizes in Fatigue MClung, R. C.
  23. 동아대학교 박사학위논문 순수Ti과 2024-T3 Al 합금의 항복응력 및 과대하중이 피로균열 진전거동에 미치는 영향 김태형