Abstract
In order to study the distribution of welding residual stress through the plate thickness. experiment and analysis of fillet welding details were carried out. Especially, a residual stress in the weld root part of T-joint fillet weld whose measurement was difficult up to now was measured. By using the heat input and the number of the weld layers as parameters, the distribution of the 3-dimensional residual stress was investigated. As a result, we can say that with increasing the heat input, the residual stress in the weld toe and weld root barely changes. But, the area of the tensile residual stress became wide. Then, comparing a single pass with multi-pass weld method, it was found that the residual stress decreased more in multi-pass than in single pass. Moreover, it was found the thing that the area of tensile residual stress by multi-pass is lower than that by single-pass in the near weld part.
용접잔류응력의 모재두께방향을 포함하는 3차원 분포를 파악하기 위해, 용접상세를 변화시킨 필렛용접이음을 대상으로 해서 실험 및 해석을 수행하였다. 특히, 지금까지 계측이 곤란했던 필렛용접이음의 용접루트부의 잔류응력을 실측하였다. 파라메타로써는 용접입열량과 용접층수를 취급하고, 모재두께방향을 포함하는 3차원 잔류응력의 분포를 조사하였다. 그 결과, 입열량이 증가하면, 용접토우와 루트부를 포함하는 용접부에서는 잔류응력의 크기에 변화가 거의 없지만, 인장잔류응력의 영역이 크게 나타났다. 또 단층과 다층용접의 비교에서는, 다층용접 쪽이 단층용접보다 잔류응력이 상당히 낮음을 알 수 있었다. 용접부 근방의 인장잔류응력의 영역도 다층용접 쪽이 단층용접보다 작게 나타난 것을 알 수 있었다.