Reforming of Propane by Carbon Dioxide using Ni/γ-A1₂O₃ Catalysts

Ni/γ-Al₂O₃ 촉매상에서 이산화탄소에 의한 프로판의 개질

Reforming of propane by carbon dioxide using NiO/${\gamma}$-$A1_2O_3$ was carried out in a pulse or continuous kid bed reactor. NiO/${\gamma}$-$Al_2O_3$ showed higher dissociation ability of $CO_2$ than NiO/${\gamma}$-$Al_2O_3$, and the former exhibited higher conversion of propane than the latter. The presence of oxygen in the reaction mixture of propane and $CO_2$ increased the conversion of propane and reduced the amount of carbon deposit on the catalyst surface. Mechanical mixture catalyst of NiO/${\gamma}$-$Al_2O_3$ and $Ga_2O_3$ showed higher stability to deactivation than NiO/${\gamma}$-$Al_2O_3$ itself. The synergistic effect between NiO/${\gamma}$-$Al_2O_3$ and $Al_2O_3$ was also observed in this study.

본 연구는 펄스 반응기 및 고정층 연속반응기를 사용하여 ${\gamma}$-알루미나에 담지된 니켈촉매상에서 이산화탄소에 의한 프로판의 개질반응 특성을 고찰한 것이다 Ni/${\gamma}$-$A1_2O_3$촉매가 NiO/${\gamma}$-$A1_2O_3$촉매보다 $CO_2$의 해리능력과 프로판의 개질 능력이 우수한 것으로 나타났다. 프로판과 $CO_2$의 혼합물에 산소를 추가한 결과 프로판의 전환율이 증가하였고 표면의 탄소침적도 감소함을 알 수 있었다. Ni/${\gamma}$-$A1_2O_3$와 $Ga_2O_3$의 기계적 혼합 촉매는 Ni/${\gamma}$-$A1_2O_3$자체보다 촉매의 활성이 오래 유지되었고 두 상의 협동에 의한 상승효과(synergistic effect)가 관찰되었다.