초록
This study evaluated shear bond strength between porcelain and resin cement according to various surface treatments of porcelain, and surface condition of debonded porcelain. 50 porcelain specimens(Celay block A2M7) and composite resin specimens(Clearfil Photo-Bright) were prepared, and divided into 5 experimental groups according to the treatment method of porcelain surface. 5 experimental groups by surface treatments were as follows; CONTROL Group : No surface treatment was done on the surface of porcelains. SAND Group : The surface of porcelains were sandblasted with $50{\mu}m$ aluminum oxide for 5 seconds. HF Group: The surface of porcelains were etched with 8% Hydrofluoric acid for 4 minutes. SIL Group: The surface of porcelains were coated with silane coupling agent and heated at $100^{\circ}C$ for 5 minutes. SAND+HF+SIL Group : The surface of porcelains were sandblasted with $50{\mu}m$ aluminum oxide for 5 seconds and etched with 8% Hydrofluoric acid for 4 minutes, and coated with silane coupling agent and heated at $100^{\circ}C$ for 5 minutes. After surface treatments on the prepared porcelain surface two pastes of Panavia 21$^{(R)}$ were mixed, they were applied between composite resin block and porcelain surface, and then excessive resin cements were removed, and its margin was surrounded with Oxyguard II. All specimens were stored for 24 hours in water at $37^{\circ}C$ and tested with Instron testing machine between porcelains and resin cements, and debonded porcelain surfaces were observed under Scanning Electon Microscope(Hitachi S-2300) at 20kvp. The values from each group were compared statistically by Student's t-test. The obtained results were as follows; 1. The shear bond strength without surface treatment of porcelain was the lowest among all experimental groups(p<0.05). 2. The detached porcelain surface with sandblasting alone had more remarkable cracks than with only Hydrofluoric Acid or Silane coupling 2gent, but showed the lowest value of shear bond strength among surface treated groups(p<0.05), 3. When porcelain surface was treated by hydrofluoric acid, it affected shear bond strength more than silane coupling agent, but there were no significant statistical differences(p>0.05). 4. When three methods were combined to increase shear bond strength between porcelains and resin cements, its value was the highest than the others(p<0.05). 5. In Scannig Electron Micrograph of detached porcelain surface with no treatment, the sample revealed adhesive failure between the porcelain and resin cement whereas detached porcelain surface with combination of three method cohesive failure on the porcelain.
(Department of Conservative Dentistry, College of Dentistry, Kyung Hee Univ.)