오스템퍼드 구상흑연주철의 기계적 성질에 미치는 Si의 영향

Influence of Si Contents on the Mechanical Properties of Austempered Ductile Iron

Influence of Si contents on the mechanical properties and microstructure of austempered ductile iron was investigated. Four different Si contents between 2.0 and 2.9% were used. Austenitizing was performed at $890^{\circ}C$ for 2 hrs and austempering temperatures were both 340 and $380^{\circ}C$ for 0.5, 1, and 2 hrs. Nodule content was more than $300/mm^2$ and nodularity was more than 90%. Microstructure was revealed using nital and retained austenite was measured by x-ray diffractometer. Tensile test, no-notch Charpy impact test and wear test were performed. Tensile strength was improved as Si content increased and both elongation and impact toughness had peak at 2.6%Si. The specimen austempered at $380^{\circ}C$ showed lower tensile strength than that of $340^{\circ}C$, but showed higher elongation. However, austempering temperature of $380^{\circ}C$ was desirable because that of $340^{\circ}C$ was close to lower bainite transformation. As austempering time increased, tensile strength and elongation were improved and optimum condition was obtained for 2 hrs heat treatment.