Machinability of Invar-type Cast Alloys

인바형 저열팽창 주조재의 절삭성

The relative machinability of the invar-type cast alloys, such as invar cast steel, invar-type cast iron, Meehanite cast iron, and the modified Invar-type cast iron containing Mo and V was evaluated based on the tool life test, the surface roughness test and the chipping test. Tool life and surface roughness were measured under various cutting conditions. The tool lives of Invar cast steel, Meehanite cast iron, the modified Invar cast iron and Invar cast iron was 12 min, 8 min, 1 min, 41 min, respectively. The surface finish of Invar cast steel and the modified Invar cast iron was better than that of Meehanite cast non, and the chip breakability of invar cast iron and Meehanite cast iron was better than that of invar cast steel. The Taylor's equations of invar cast steel and the modified invar cast iron were $VT^{0.3076}=154.479$ and $VT^{0.3880}=102.326$, respectively. As the cutting speed increases, the surface finish of the modified invar cast iron was improved.