A Study on Deep Levels in Rapid Thermal Annealed PICTS Semi-Insulating InP(100) by PICTS

PICTS 방법에 의한 급속열처리시킨 반절연성 InP(100)에서 깊은준위에 관한 연구

The behavior of de levels in rapid thermal annealed Fe-doped semi-insulating InP(100) was studied by photoinduced current transient spectrocopy(PICTS). In bulk InP, T2(Ec-0.24 eV), T3(Ec-0.30 eV) and T5(Ec-0.62 eV) traps were observed. After annealing the T2 trap was annihilated at 20$0^{\circ}C$ and recreated at 35$0^{\circ}C$. T3 trap was not affected below 40$0^{\circ}C$. With increasing temperature the concentration of T5 trap reduced and it was annihilated at 30$0^{\circ}C$. However the T1(Ec-0.16 eV) and T4(Ec-0.42 eV) traps were began to appear at 40$0^{\circ}C$and these concentrations were increased with annealing temperature. The T1 and T4 traps seem to be related to the isolated phosphorus vacancy( $V_{p}$) and $V_{p}$-indium antisite( $V_{p}$- $P_{in}$ ) or $V_{p}$-indium interstitial( $V_{p}$-I $n_{I}$) respectiely.respectiely.