Abstract
The magnetoresistance and the saturation field behavior of the Co-Ag nano granular films as a function of the composition and the ferromagnetic underlayer and overlayermaterials were investigated. The maximum magnetoresistance of 23% and the saturation field of 2.3 kOe at room temperature were obtained in the as-deposited 3000$\AA$ $Co_{30}Ag_{70}$ single alloy films. The magnetoresistance and the saturation field of 100$\AA$ $Co_{30}Ag-{70}$ alloy film were 3.65 % and 3.0 kOe respectively. Those of the sandwiched films with 200$\AA$ Fe were 3.3 % and 1.23 kOe respectively. The saturation field of the sandwiched alloy films could be reduced by the exchange coupling between the ferromagnetic layers and the alloy layer. The effective depth of the exchange coupling was approximately 150$\AA$ in each Fe layer. Among the Fe, Co, and FeNi, the most effective materials to reduce the saturation field of the sandwiched alloy films was Fe.
조성과 강자성 상하지층이 Co-Ag 나노입상 합금박막의 거대자기저항과 포화자기장에 미치는 효과에 대하여 연구하였다. 두께 3000 .angs. , 30 at.% Co 조성의 증착된 상태의 합금박막에서 23 %의 최대 자기저항비를 얻었으며 포화자기장은 2.3 kOe 였다. 두께 .angs.의 $Co_{30}$Ag$_{70}$ 합금박막의 자기저항비는 3.65 %, 포화자기장은 3.0 kOe 이었으며 200 .angs. 의 Fe를 상하지층으로 증착하였을 때 자기저항비는 3.3%, 포화자기장은 1.23 kOe로 감소하였다. 강자성 상하지층이 교환결합에 의하여 합금박막의 포화자기장을 감소 시키는 효과가 있었으며 그 효과는 합금박막의 두께가 약 3000 .angs. 이하에서 나타났다. 교환결합 강자성체 인 Co, NiFe, 그리고 Fe중에서 포화자 기장 감소에 가장 효과적인 재료는 Fe 이었다.다.