Abstract
Amorphous $Fe_{50}Zr_{50}$ alloy has been manufactured by mechanical alloying from pure elemental powders of Fe and Zr in conventional ball mill under an Ar atmosphere. Structure and magnetic properties of the amorphous phase were studied by transmission electron microscopy and SQUID magnetometry. Selected area diffraction patterns taken from the mechanically alloyed powders showed two halo rings, indicating coexistence of Fe rich and Zr rich amorphous phases in mechanically alloyed powder. Curie temperature of the Fe rich amorphous phase, measured by Arrot plot, was 195 K. Fe content in the ferromagnetic amorphous phase, estimated from the Curie temperature, was about 65 at%. Spin wave stiffness constant of $Fe_{50} Zr_{50}$ alloys processed for 100 and 200 hrs were 52.2 and 63.8 meV, respectively. The higher spin wave stiffness constant in 200 hrs milled powders may arise from the precipitation of $\alpha$-Fe by partial crystallization of amorphous phase.
회전형 볼밀을 이용하여 Ar 분위기에서 기계적 합금화 방법으로 Fe$_{50}$Zr$_{50}$ 비정질을 제조하고 이들의 구조 및 자기적 성질을 투과전자현미경과 SQUID 자력계를 이용하여 조사하였다. 기계적합금화법으로 제조된 분말로 부터 얻은 제한시야 회절도형은 두개의 인접한 halo ring 도형을 나타내며, 이것은 비정질이 Fe rich 한 비정질과 Zr rich 한 두 비정질로이 공존하기 때문이다. 기계적 합금화한 Fe$_{50}$Zr$_{50}$ 비정질 분말에서 비정질상의 큐리온도로 부터 추정된 강자성 Fe-Zr계 비정지상의 Fe 조성은 100시간 합금화한 경우 65 at% 로서, 이것은 비정질의 상분리가 일어났기 때문이며, 이 결과는 회절도형의 분석결과와 일치한다. 기계적 합금화한 Fe$_{50}$Zr$_{50}$ 분말의 스핀파 탄성계수는 100시간 합금화한 경우에는 52.2 meV .angs. 이고, 200시간 합금화 한 경우에는 63.8 meV .angs. 으로 합금화시간이 증가함에 따라 증가하였다. 이것으 200시간 합금화한 경우 부분 결정화에 의하여 .alpha. -Fe가 일부 석출하였기 때문이다.