Abstract
The performance of The performance of $Li/V_6O_{13}$ cell and the electrochemical properties of polymer electrolyte based on poly(acrylonitrile)[PAN] was investigated. The ionic conductivity of polymer electrolyte showed $2.3{\times}10^{-3}S/cm$ and the compatibility with lithium electrode was excellent. Also, it showed the electrochemical stability up to 4.3V(vs. $Li^+/Li$). The cell reaction of $Li/V_6O_{13}$ was dominated by the interfacial resistance between $V_6O_{13}$ electrode and polymer electrolyte. The diffusion coefficient of lithium ion within $V_6O_{13}$ was $2.7{\times}10^{-9}{\sim}4.2{\times}10^{-8}cm^2/sec$. The utilization of $V_6O_{13}$ active material was 95% at C/8($50{\mu}A/cm^2$) and 82% at C/4($100{\mu}A/cm^2$), respectively.
$Li/V_6O_{13}$ 전지의 성능과 poly(acrylonitrile)[PAN]계 폴리머 전해질의 전기화학적인 성질을 조사 하였다. 폴리머 전해질의 이온 전도도는 상온에서 $2.3{\times}10^{-3}S/cm$를 보였으며 리튬 전극과의 상용성도 우수하였다. 또한 4.3V(vs. $Li^+/Li$)까지의 전기화학적인 안정성이 있는 것으로 나타났다. $Li/V_6O_{13}$ 전지 반응은 $V_6O_{13}$ 전극과 폴리머 전해질간의 계면 저항이 지배적 이었다. $V_6O_{13}$내의 리튬 이온의 확산 계수값은 $2.7{\times}10^{-9}{\sim}4.2{\times}10^{-8}cm^2/sec$로 나타났다. $V_6O_{13}$ 활물질의 이용률은 C/8($50{\mu}A/cm^2$)에서 95%였으며 C/4($100{\mu}A/cm^2$)에서는 82%로 각각 나타났다.