Cure Kinetics of DGEBA/MDA/HQ-PGE System

DGEBA/MDA/HQ-PGE계의 경화 반응 속도론

  • 송영욱 (서울시립대학교 공과대학 화학공학과) ;
  • 심미자 (서울시립대학교 문리과대학 생명과학과) ;
  • 김상욱 (서울시립대학교 공과대학 화학공학과)
  • Received : 1995.12.29
  • Accepted : 1996.01.30
  • Published : 1996.04.10

Abstract

Cure kinetics of diglycidyl ether of bisphenol A(DGEBA)/4,4'-methylene dianiline(MDA) with hydroquinone-phenyl glycidyl ether(HQ-PGE) as a reactive additive, which was preliminarily synthesized, was investigated by DSC and FT-IR analyses. Kissinger equation and Arrhenius' equation were used to calculate activation energy and pre-exponential factor. When HQ-PGE was added to DGEBA/MDA system, it reduced activation energy of system. When the 5 phr of HQ-PGE was added to DGEBA/MDA system, activation energy was 7.8 kcal/mol by FT-IR analysis and 11.3 kcal/mol by DSC, in comparison with the system without HQ-PGE, activation energy decreased about 30% and 9%, respectively. According to these results, HQ-PGE, introducing agent of this system, acted as a catalyst.

반응성 첨가제로 HQ와 PGE를 합성시킨 HQ-PGE를 사용하여, DGEBA/MDA계의 경화반응이 일어날 때의 속도론을 DSC와 FT-IR을 이용하여 조사하였다. 그리고, Kissinger equation과 Arrhenius equation을 이용하여 활성화 에너지와 pre-exponential factor 값을 구하였다. 계의 활성화 에너지는 HQ-PGE가 첨가되었을 때 감소하였다. 합성 HQ-PGE가 5 phr 첨가되었을 때, DGEBA/MDA계의 활성화 에너지는 FT-IR로 측정하였을 때 7.8 kcal/mol, DSC로 측정하였을 때에 11.3 kcal/mol을 나타내었다. 이 값은 HQ-PGE가 첨가되지 않은 경우보다 각각 30%, 9% 감소된 값이었다. 이 결과들을 통해서 반응성 첨가제로 사용된 HQ-PGE는 본 계에서 촉매의 역할을 함을 알 수 있었다.

Keywords

Acknowledgement

Supported by : Sun Kyong group

References

  1. Polym. Eng. Sci. v.27 S. N. Lee;W. B. You
  2. J. Appl. Polym. Sci. v.33 M. R. Keenan
  3. J. Korean Ind. & Eng. Chem. v.5 I. S. Chun;M. J. Shim;S. W. Kim
  4. Mater. Chem. & Phys. v.44 J. Y. Lee;M. J. Shim;S. W. Kim
  5. J. Appl. Polym. Sci. v.29 R. E. Smith;F. N. Larsen;C. L. Long
  6. Polym. Eng. and Sci. v.27 C. S. Chern;G. W. Poehlein
  7. Polym. Eng. and Sci. v.22 T. Donnellan;D. Roylane
  8. J. Appl. Polym. Sci. v.29 A. Sabra;J. P. Pascault;G. Seytre
  9. Polym. Mater. Sci. Eng. v.51 E. T. Mones;R. J. Morgan
  10. Mater. Res. v.2 S. W. Cho;M. J. Shim;S. W. Kim
  11. Proceed. IUMRS-ICA-'94 J. Y. Lee;M. J. Shim;S. W. Kim
  12. J. Korean Ind. & Eng. Chem. v.5 J. Y. Lee;M. J. Shim;S. W. Kim
  13. J. Korean Ind. & Eng. Chem. v.5 M. J. Shim;S. W. Kim
  14. J. Korean Ind. & Eng. Chem. v.5 J. Y. Lee;M. J. Shim;S. W. Kim
  15. Thermal Characterization of Polymeric Materials E. A. Turi