Abstract
In this paper, we investigated the retention amounts(ash contents) according to the addition amounts of retention aid and calcium carbonate and compared the mechanical and optical properties of sheets under the same ash content. As the addition amounts of retention aid increase, the retention of calcium carbonate, that is, ash contents of sheets increase in all retention system. In this case, the sheets included ash content as already expected is produced by adjusting the addition amounts of retention aid and calcium carbonate. Tensile index, burst index, tear index, internal bonding strength of sheets straightly decrease as the ash content of sheets increases. Especially, in the same ash content, all sorts of strength are high in compozil system, low in dual polymer system. Opacity increases along with according to the increase of ash content, and is high in hydrocol system, the worst in dual polymer system. In equal opacity, the strength of paper decreases compozil, hydrocol, and dual polymer system in order. But to judge she superiority or inferiority of retention aids, it should consider the various factors such as the optimum production and process conditions besides the retention amounts of filler and the sheet strength.
본 실험에서는 보류향상제의 첨가량과 중질 탄산칼슘 첨가량에 따른 탄산칼슘 보류량(회분함량)을 조사하였으며, 동일 회분량에서 종이의 기계적 광학적 특성을 비교하였다. 각 보류시스템 모두 보류향상제 첨가량을 증가시키면 중질 탄산칼슘(입자평균직경 $3.2{\mu}m$) 보류, 즉 종이의 회분량은 증가한다. 이 경우 보류향상제와 중질 탄산칼슘 첨가량을 조절하여 이미 예정된 회분량이 함유된 종이를 초지할 수 있다. 종이의 인장지수, 파열지수, 인열지수 및 내부결합강도는 종이의 회분량이 증가됨에 따라 직선적으로 감소한다. 특히 동일 회분량에서 비교하면, 콤포질 시스템에 의한 종이에서 제반 강도가 높고, 듀알 폴리머 시스템에서는 강도가 낮다. 불투명도는 회분량 증가에 따라 함께 증가하며, 하이드로콜 시스템에서 가장 높고 역시 듀알 폴리머에서 가장 낮다. 동일 불투명도에서 종이의 강도는 콤포질, 하이드로콜, 듀알 폴리머 시스템 순으로 감소한다. 그러나 보류향상제의 우열을 판단하기 위해서는 충전제의 보류량과 종이의 강도 이외에도 적정 생산조건 및 적정 공정조건과 같은 여러 가지 다른 요인들도 고려되어야 한다.