Abstract
Electrochemical characteristics and physical properties of polymer electrolyte which immobilized lithium salts such as $LiClO_4$ and $LiCF_3SO_3$ and plasticizers such as ethylene carbonate(EC) and propylene carbonate(PC) in high molecular weight poly(ethylene oxide)[PEO] polymer was investigated. PEO-Li based polymer electrolyte with plasticizers showed ionic conductivity of $10^{-4}S/cm$ at room temperature and high electrochemical stability up to 4.5 V(vs. $Li^+/Li$), so it can be applied to lithium secondary battery. The crystallinity of PEO decreased with the addition of lithium salts and plasticizers, especially $LiClO_4$ and PC showed more effective than and $LiCF_3SO_3$ and EC. Glass transition temperature($T_g$) of polymer electrolyte increased with increasing lithium salt concentration whereas melting temperature ($T_m$) decreased. Polymer electrolyte with plasticizers crystallized at $6^{\circ}C$.
분자량이 큰 Poly(ethylene oxide)[PEO] 고분자에 $LiClO_4$, $LiCF_3SO_3$ 등의 리튬염과 ethylene carbonate(EC), propylene carbonate(PC) 등의 가소제를 고정화시킨 고분자 전해질의 전기화학적 특성 및 물리적 성질을 조사하였다. 가소제가 첨가된 PEO-Li계 고분자 전해질은 상온에서 $10^{-4}S/cm$의 이온 전도도를 보였고 4.5 V(vs. $Li^+/Li$)까지 높은 전기화학적인 안정성을 나타냄으로써 리튬 2차전지에 적용 가능한 것으로 나타났다. 리튬염 및 가소제의 첨가에 따라 PEO의 결정상이 감소되었고 특히 $LiClO_4$, PC등이 $LiCF_3SO_3$, EC 등에 비하여 더 효과적인 것으로 나타났다. 리튬염의 농도가 증가할수록 고분자 전해질의 유리전이온도($T_g$)는 증가되었으며 반면에 융점온도($T_m$)는 감소하는 것으로 나타났다. 가소제가 첨가된 고분자 전해질은 $6^{\circ}C$에서 결정화 되었다.
