Abstract
This study represents the synthetic characteristics of styrene-DVB copolymer which is used as a catalyst support for the removal of tritium in CANDU. To evaluate the effect of solvent on the styrene-DVB polymeric support, the solvating power dependent on various kinds and composition of solvents was calculated. In order to synthesize the macroreticular type polymer bead, the following conditions are needed; solvating power should be higher than 1 for 20% of crosslinkage and higher than 3 for 40% of crosslinkage. Stabilization of organic monomers at about $40^{\circ}C$ for more than 2 hours is prerequisite. Removal of solvent prior to drying is preferred for the post-treatment of the bead. The polymer particle size was increased by lowering concentration of surfactant and stirring speed.
중수형 발전소에서 삼중수소 제거 공정에 이용되는 소수성 고분자촉매의 담체인 스티렌-디비닐벤젠 공중합체의 제조 특성을 실험하였다. 스티렌-디비닐벤젠 고분자담체의 제조시 담체의 표면 특성에 대한 용매의 영향을 고찰하기 위하여 일정한 용매계에서 용매비를 변화시켜 solvating power 값을 구하였다. 거시기공 형태의 담체가 제조되기 위한 solvating power는 가교도가 20%일 때 3 이상, 가교도가 40%일 때는 1 이상의 값이 필요하였으며 약 $40^{\circ}C$에서 2시간 이상 용액의 안정이 필요하였다. 또한 후처리 방법은 담체를 건조시키기 전에 용매를 제거하는 방법이 가장 우수한 기공 특성을 나타내었다. 담체의 입자 크기는 교반속도 및 계면활성제의 농도가 낮을수록 더 크게 생성됨을 알 수 있었다.