수종 근관 충전용 시멘트의 조직반응에 관한 조직학적 연구

HISTOLOGIC STUDY OF THE TISSUE RESPONSE TO THREE ROOT CANAL CEMENTS

  • 조용범 (단국대학교 치과대학 보존학교실)
  • Cho, Yong-Bum (Dept. of Conservative Dentistry, School of Dentistry, Dankook University)
  • 발행 : 1996.10.31

초록

This study was conducted to evaluate the tissue responses histologically to three root canal cements : Sealapex, AH-26, and zinc oxide-eugenol cement. Twelve white female Sprague-Dawley rats, weighing between 350 and 400 gm, were anesthetized with an intraperitoneal injection of Ketamine hydrochloride(0.4 ml). After shaving the sites selected(left and right scapular areas, left and right pelvic areas), the animal's backs were scrubed with soap and water, and sterilized with absolute alcohol. Each material was mixed to a thin consistency to flow out easily through a 24-guage needle, and loaded into a sterile, disposable plastic 1-ml syringe. All of the rats were injected subcutaneously with 0.1 ml of the three test sealers. Normal saline was used as a control. Animals were sacrificed after 48hr, 1, 4, and 12 weeks by overanesthetization using jars containing anesthetic ether. The tested sites were surgically removed with the surrounding tissue and fixed with 10% formalin. After 48 hours specimens were embedded in paraffin, sectioned to an average thickness of $6{\mu}m$ thick, stained with hematoxylin-eosin. The slides were examined under the light microscope. The results were obtained as follows 1. All material except the control showed various degree of inflammation on 48 hr. 2. Sealapex : In early stage, severe inflammatory cell infiltration was observed. At the 4th weeks observation, graunlomatous tissue with macrophage and foreing body giant cells containing many dark particles in their cytoplasm was observed. 3. AH-26 : Mild inflammatoy reaction was observed with AH-26 throughout the experimental period. 4. Zinc oxide-eugenol cement : Severe inflammatory cell infiltration, necrosis along the material, edema could be seen in early stage. Zinc oxide-eugenol cement maintained a moderate/severe reaction throughout the experimental period.

키워드