Abstract
The purpose of this study was to evaluate the adaptability to tooth structure of composite resin and glass ionomer cement according to filling methods. In this study. two class V cavities were prepared on the buccal and lingual surface of each tooth of forty extracted human premolars. and they were randomly assigned into 4 groups with 10 teeth. The cavities of each group were filled with the CLEARFIL FII self curing resin(Control Group), Z-100 light curing resin (Group 1). $Vitremer^{TM}$ light curing glass ionomer cement(Group 2) and Z-100 light curing resin over the $Vitremer^{TM}$ liner(Group 3). The specimens underwent temperature changed from $5^{\circ}C$ to $55^{\circ}C$ five hundred times. After thermocycling. specimens were immersed in 2% methylene blue solution and stored in 100% relative humidity at $37^{\circ}C$ for 24 hours. And then. the specimens sectioned buccolingually. Degree of dye penetration at tooth-restoration interfaces were examined by Tool maker's microscope(x 200) and Image analyzer. The results were as follows : 1. On the occlusal margin. among the experimental groups. the group 2 showed the highest dye penetration($2.40{\pm}0.68$) and the group 3 showed the lowest dye penetration($1.15{\pm}0.37$). There was significant difference among the experimental groups(p<0.001). 2. On the gingival margin, among the experimental groups, the group 1 showed the highest dye penetration($3.30{\pm}0.57$) and the group 2 showed the lowest dye penetration($1.65{\pm}0.49$). There was significant difference among the experimental groups(p>0.001). 3. About total degree of dye penetration, the group 1 showed the highest dye penetration($2.25{\pm}1.17$) and the group 3 showed the lowest dye penetration ($1.43{\pm}0.55$). There was significant difference among the experimental groups(p<0.001). 4. The sum of dye penetration at occlusal margin was less than gingival margin. There was significant difference between occlusal margin and gingival margin (p<0.001). The results showed that differences were more pronounced at the gingival margin. Composite restorations inserted over the glass-ionomer liner demonstrated significantly less leakage than single restoration that used composite resin or glass-ionomer cement.