DIMENSIONAL STABILITY OF ELASTOMERIC IMPRESSION MATERIALS USING HOLOGRAPHIC INTERFEROMETRY

Holographic Interferometry를 이용한 탄성 고무 인상재의 체적변화에 관한 연구

  • Ha, Chee-Yang (Department of Prosthodontics, School of Dentistry, Kyung Hee University) ;
  • Lee, Sung-Bok (Department of Prosthodontics, School of Dentistry, Kyung Hee University) ;
  • Woo, Yi-Hyung (Department of Prosthodontics, School of Dentistry, Kyung Hee University)
  • 하치양 (경희대학교 치과대학 보철학 교실) ;
  • 이성복 (경희대학교 치과대학 보철학 교실) ;
  • 우이형 (경희대학교 치과대학 보철학 교실)
  • Published : 1996.09.01

Abstract

This study investigated the time-dependent dimensional changes of elastomeric impression materials using holographic interferometry. Six commercial impression materials, Permlastic(polysulfide), Xantopren VL (condensation silicone), low and medium viscosity of Exafine, Provil (addition silicone), and Impregum(polyether), were selected. Steel plate was used as custom tray, and each impression specimen was 20 mm in width, 15 mm in length and 3 mm in thickness. Each impression material was evaluated at 30 minutes, 1, 2, 4, 6, 8 and 12 hours after setting using real-time holography. The results were as follow : 1. Xantopren VL and Permlastic showed relatively severe and continuous dimensional changes after setting. Low viscosity of Exafine, Provil, Impregum showed relatively slight dimensional changes with function of time and medium viscosity of Exafine showed almost no dimensional change from 2 hours after setting to 6 hours. 2. On initial dimensional changes within 1 hour, the amount of change in low viscosity of Exafine was the least and Xantopren VL was the largest. 3. On dimensional changes at 4 hours after setting, the amount of change in medium viscosity of Exafine was the least and tile change of Xantopren VL was the largest. 4. In overall dimensional stability during 12 hours, medium viscosity of Exafine was the most stable and Xantopren VL and Permlastic were least stable.