Application of Hepatocyte Specific Polymers with Functional group

기능성 고분자의 세포특이성 재료로의 이용에 관한 연구

New hepatocyte specific copolymers, that have oligosaccharide and biotin residue on the side chain of styrene, were designed and synthesized to use as a multifunctional recognition. In order to measure initial adhesion efficiency, 1mL of copolymer solutions (0.01%, w/v) such as p(VLA-co-VBA) 90 : 10, p(VLA-co-VBA) 80 : 10 and PYLA as a standard were added to polystyrene petri dish, respectively. In the absence and presence of serum, hepatocyte solution of rat by method of Seglen was added. After 60 min, adhesion efficiency was 70%, that is similar to those of the absence of serum. Aggregation capacity between biotin residue in p(VLA-co-VBA) 70 : 30 and avidin was measured by using UV-transmittance.

본 연구에서는 스티렌 골격에 올리고당 및 비오틴 잔기를 결사슬에 갖는 새로운 세포 특이성 고분자 재료를 설계하여 합성하였다. 이들 고분자 재료를 간세포의 다점 인식 재료로서의 사용 가능성을 검토한 실험 결과를 보고하고자 한다. 간세포의 초기 접착 거동을 조사하기 위하여 합성된 고분자 재료 p(VLA-co- VBA) 90 : 10, p(VLA-co-VBA) 80 : 20 및 대조 물질로 PVLA의 농도가 각각 0.01%(w/v) 되도록 조절하여 1mL 씩 폴리스티렌 페트리 접시에 넣고, 혈청 존재 및 비존재하에서 Seglen법으로 단리한 간세포를 각각 첨가한 결과 60분 경과 후에는 혈청 비존재하에서와 같은 70% 정도의 높은 접착률을 보여 주었다. 폴리머 p(VLA-co-VBA) 70:30에 함유된 비오틴 잔기와 아비딘과의 분자 회합에 의한 응집형상은 UV 투과율의 변화로 확인 하였다.