Electrochemical Impedance Analysis of Polyaniline-Film on Tungsten Electrodes

텅스텐 전극에 입힌 폴리아닐린의 전기화학적 임피던스

  • 천정균 (한국외국어대학교 자연과학대학 화학과) ;
  • 민병훈 (동양화학주식회사 중앙연구소)
  • Published : 19960100
Download PDF
⟨ Previous Next ⟩

Abstract

The electrochemical impedance spectra of polyaniline film coated on tungsten electrodes by cyclic voltammetry have been measured in 0.1 M aqueous sulfuric acid solution. An electrochemical cell composed of large redox capacitance and low resistance of PANI-film in series was in agreement with the conductive behavior reported at these potentials. When the PANI was coated on bare tungsten, the electrolytic resistance was only observed. However, on the oxidized tungsten instead of bare tungsten, the resistance of tungsten oxide and the contact resistance between PANI and tungsten oxide were additionally observed. Equivalent electrical circuits have been deduced from the impedance data. It was therfore possible to obtain the parameters of the ionic mass transport within the film.

텅스텐을 작업 전극으로 사용하여 순환 전압-전류법으로 합성한 폴리아닐린 막의 전기화학적 임피던스를 0.1M 황산 용액에서 측정하였다. 전기 전도성을 갖는 퍼텐셜 영역에서는 고분자 막의 큰 축전-용량과작은 저항이 직렬로 연결된 전기화학 쎌이 관측되었다. 순수한 텅스텐에 입혀진 폴리아닐린은 접촉 저항을 무시할 수 있었으나, 산화 전극 막이 입혀진 텅스텐의 경우는 산화 전극 막의 저항과 접촉 저항이 관측되었다. 측정된 임피던스 데이터로부터 전극의 등가 회로를 추정하였으며, 이 등가 회로를 토대로 하여 폴리아닐린-막 안에 혼입된 이온의 물질 이동 파라미터를 산출하였다.

Keywords

References

  1. Advances in Electrochemical Science and Engineering v.1 Evans, G. P.;Gerisher, H.(ed.);Tobias, C. W.(ed.)
  2. References in Ref. v.1 Evans, G. P.
  3. J. Electrochem. Soc. v.133 Nagasubramanian, G.;Distefano, S.;Moacanin, J.
  4. J. Electrochem. Soc. v.136 Osaka, T.;Naoi, K.;Maeda, M.;Nakamura, S.
  5. J. Electrochem. Soc. v.139 Miller, D. L.;Bockris, J. O.
  6. J. Electrochem. Soc. v.111 Diaz, A. F.;Logan, J. A.
  7. J. Electroanal. Chem. v.177 Kobayashi, T.;Yoneyama, H.;Tamura, H.
  8. J. Electroanal. Chem. v.195 Genies, E. M.;Tsintavis, C.
  9. J. Electroanal. Chem. v.209 Kitani, A.;Yano, J.;Sasaki, K.
  10. Synth. Metals v.18 MacDiarmid, A.;Yang, L. S.;Huang, W. S.;Humphry, B. D.
  11. J. Electrochem. Soc. v.135 Lacroix, J.-C.;Diaz, A. F.
  12. J. Electrochem. Soc. v.135 Stilwell, D. E.;Park, S.-M.
  13. J. Electrochem. Soc. v.135 Stilwell, D. E.;Park, S.-M.
  14. J. Electroanal. Chem. v.235 Zotti, G.;Carttarin, S.;Comisso, N.
  15. J. Electroanal. Chem. v.239 Zotti, G.;Carttarin, S.;Comisso, N.
  16. Electrochim. Acta v.34 Nunziante, P.;Pistoia, G.
  17. Bull. Korean Chem. Soc. v.9 Chon, J.-K.;Kim, J.-D.
  18. Bull. Korean Chem. Soc. v.11 Chon, J.-K.;Min, B.;Paik, W.
  19. J. Korean Chem. Soc. v.38 Chon, J.-K.;Min, B.
  20. J. Electrochem. Soc. v.134 Glarum, S. H.;Marshall, J. H.
  21. J. Electrochem. Soc. v.133 Rubinstein, I.;Rishpon, J.;Gottesfeld, S.
  22. J. Electrochem. Soc. v.134 Rubinstein, I.;Sabatani, E.;Rishpon, J.
  23. Electrochim. Acta v.34 Fiordiponti, P.;Pistoia, G.
  24. Electrochim. Acta v.39 Genz, O.;Lohrengel, M. M.;Schultze, J. W.
  25. Electrochim. Acta v.39 Grzeszczuk, M.
  26. J. Appl. Electrochem. v.24 Biazzio, S. R.;Oliveira, C. L. I.;Aguirre, M. J.;Zagal, J. H.
  27. J. Korean Chem. Soc. v.39 Chon, J.-K.;Min, B.
  28. Electrochim. Acta v.39 Gao, Z.;Kvranstrom, C.;Ivaska, A.
  29. Electrochim. Acta v.40 Barbero, C.;Tucceri, R. I.;Posadas, D.;Silver, J. J.;Sereno, L.
  30. Syn. Met. v.18 Tanguy, J.;Mermilliod, N.;Hoclet, M.