Synthesis of Cement Raw Materials by Melting of Industrial Wastes

폐기물의 용융처리에 의한 시멘트원료의 합성

CZS(2Ca0 , SiO\ulcorner) phase of cement clinkcr was obtaincd by melting mixcd four indnstrial wasles of limestone sludge, waste Foundry sand, coal lly ash fiorn power plants and chernicas glasses. The effect ot mixing ratio of four rvastc mater~als ou the composnlg phascs in melled slag was investigated. Thc mixed wastes were meltcd to slag by heat under a constant basicity at 1370C. The shg consisted of p -CIS and C,AS(2CaO - A I P , . SiO,). The ratio of two phases was varied with mixing ~atioo f the waste materials. In order Lo increasc the amount ot j -C2S phase, the coal fly ash content should be reduced, while amount of the chemical glass be increased. The coal fly ash contcnt was the most imporlant factor in controlling phases of thc melted-slag.

석회석슬럿지, 폐주물사, 석탄회 및 폐유리병 등의 산업폐기물을 용융처리하여 시멘트 클링커 상의 일부인 $C_2$S(2CaO.$SiO_2$)를 얻고, 폐기물 원료의 배합비율을 변화시킬 때 각 폐기물의 최종 생성물에 미치는 영향을 조사하였다. 일정한 염기도를 갖도록 혼합된 폐기물을 $1370^{\circ}C$에서 용융 처리한 결과 $\beta$-C$_2$S 및 $C_2$AS(2CaO.$Al_2$$O_3$.$SiO_2$)상으로 이루어진 용융물을 얻을 수 있었고, 2가지 상의 분율은 폐기물 원료의 조합방법에 따라 변하였다. 직교배열표를 이용하여 각 폐기물의 함량이 최종 용융물의 상에 미치는 영향을 조사한 결과, $\beta$-$C_2$S 상의 분율을 증가시키기 위해서는 석탄회의 함량을 감소시키고 폐유리병의 함량을 증가시켜야 함이 밝혀졌다. 분산분석을 행한 결과 석탄회의 함량조절이 최종 용융물의 상을 조절하는데 있어서 가장 중요한 인자임을 알 수 있었다.