Abstract
The characteristics of the complex permeability of ${(Ni_{x}Cu_{0.2}Zn_{0.8-x}O)}_{1-w}{(Fe_{2}O_{3})}_{1+w}$ with various Ni and $Co_{3}O_{4}$ contents were investigated in this work. It is found that the NiCuZn ferrites with $x{\geq}0.6$ have a relatively small peak width of the imaginary part of permeability $\mu$". The resonance frequency is increased as Ni content becomes higher, where the loss is low. The $\mu$" value decreases with increasing FezO, deficiency, but the resonance frequency($f_{\mu"max}$) is only slightly affected by $Fe_{2}O_{3}$ deficiency. In case of $Co_{3}O_{4}$ addition to the NiCuZn ferrites, the $f_{\mu"max}$ increases since the initial permeability decreases with the amount of $Co_{3}O_{4}$. It is concluded that the Ni content in the NiCuZn ferrite is a dominant factor for the total loss of these spinel ferrites.
본 연구에서는 ${(Ni_{x}Cu_{0.2}Zn_{0.8-x}O)}_{1-w}{(Fe_{2}O_{3})}_{1+w}$의 Ni 함량(x)과 $Co_{3}O_{4}$ 첨가량에 따른 복소투자율 변화에 관하여 검토하였다. Ni 함량 x=0.6 이상에서는 매우 좁은 투자율 허수항($\mu$") 피이크가 형성됨으로서 다른 조성에 비해 손실이 적음을 알 수 있었고 공명주파수($f_{\mu"max}$)는 Ni 함량의 변화와 비례하여 현저하게 증가하였다. $Fe_{2}O_{3}$ 결핍량(w)이 많을 수록 $\mu$" 값은 낮았으나, $Fe_{2}O_{3}$ 결핍량(w)의 변화가 공명주파수에는 큰 영향을 미치지 않는 경향을 나타내었다. NiCuZn 페라이트 조성에 대하여 $Co_{3}O_{4}$를 첨가한 경우는 첨가량이 많아짐에 따라 초기투자율이 감소하여 $f_{\mu"max}$ 값은 증가하였으나, 전체적인 손실의 정도를 제어하는데에는 Ni 함량을 변화시키는 것이 더 효과적임을 알 수 있었다.