Abstract
To obtain the Pr-Fe-B ternary system magnets with higher $(BH)_{max}$, the effect of composition ratio and various heat-treatment temperatures on the magnetic properties of Pr-Fe-B system rare-earth magnets were investigated. The magnets with various composition of Pr and Fe were heat-treated at $990^{\circ}C$, $625^{\circ}C$, $585^{\circ}C$, $550^{\circ}C$ after sintering. Curie temperature is $310^{\circ}C$ and quantitative analysis by SEM, EDX shows that the $Pr_{2}Fe_{14}B$, Pr-rich phase consist of Pr~14 at.% and Fe~86 at.%, Pr~58 at.% and Fe~42 at.%, respectively. The coercivity is decreased after heat-treating at $990^{\circ}C$ and increased from 5.6 to 6.3 kOe at $625^{\circ}C$. The maximum energy product is decreased from 43.4 to 30.3 MGOe after the heat-treating at $990^{\circ}C$ but increased from 42.7 to 45.0 MGOe, about 5 %, by heat-treating at $625^{\circ}C$.
보자력과 최대 에너지적이 높은 Pr-Fe-B 3원계 자석을 얻는 것을 목적으로 하여, 조성비와 열처리 온도의 변화에 따른 각 자석의 자기적 특성을 조사하였다. Pr과 Fe의 조성을 달리하여 자석을 만들고 소결 후 $550^{\circ}C$, $585^{\circ}C$, $625^{\circ}C$, $990^{\circ}C$에서 열처리를 하였다. 각 자석의 큐리온도는 $310^{\circ}C$이었고, SEM과 EDX 분석 결과, 주상인 $Pr_{2}Fe_{14}B$상은 14 at.%의 Pr과 86 at.%의 Fe, 미소상인 Pr-rich상은 58 at.%의 Pr과 42 at.%의 Fe로 이루어져있었다. 보자력은 $990^{\circ}C$에서의 열처리 후에 현저히 감소하였고 $550^{\circ}C$, $585^{\circ}C$, $625^{\circ}C$에서의 열처리 후에는 모두 증가하였는데 특히 $625^{\circ}C$에서의 열처리 후에 5.6에서 6.3 kOe로 향상되었다. 열처리 온도에 대한 최대에너지적의 변화는 보자력의 변화와 거의 같은 경향을 보였고, $625^{\circ}C$에서의 열처리 후에 최대 에너지적을 42.7에서 45.0 MGOe로 약 5% 향상시킬 수 있었다.