Abstract
In thick film resistors, the characteristics of the frit and the reaction between glass frit and conductor material play an important role for their electrical properties. In this study, various glass frits in the system of $60RO{\cdot}20SiO_2$ $15B_2O_3{\cdot}5Al_2O_3$(RO=PbO, ZnO, CdO; mole%) were mixed with $RuO_2$ and coated on 96% alumina substrate. Only the glass frit containing PbO was reacted with $RuO_2$in$RuO_{2+}$-thick film resistor and produced the new crystalline phase of $Pb_2Ru_2O_{65}$. Their electrical resistivities strongly depend on the amount of $Pb_2Ru_2O_{65}$ crystalline phase obtained, which varied with firing temperature. The sheet resistivities of these resistors were varied from $10^3\; to\; 10^6\;{\Omega}/{\Box}$ depending on heat treatment, and the absolute value of TCR was decreased as the heat treatment temperature increaed. However, $RuO_2$ did not reacted with the glass frits containing ZnO nor CdO, and the resulting showed very high sheet resistivities.