Applicability of SiC coating through CVD process and PCS(polycarbosilane) impregnation for the oxidation resistance and mechanical properties of C/C composite was studied. The SiC layer coated by CVD was deposited uniformly on the C/C composite, whereas the SiC converted from PCS impregnation wetted around individual carbon fiber. The PCS-impregnated C/C composite exhibited a significant increase of bending strength in comparison with as received C/C composite. This increase in the mechanical property could be attributed to the high bonding strength between fibers due to an impregnated SiC phase. The PCS-impregnated C/C showed 25% improvement in density, 3.5 times higher MOR and 2.8 times higher oxidation resistance compared to the as-received C/C. The increments due to PCS impregnation were more effective than CVD process.
본 연구에서는 탄소/탄소 복합체의 내산화성을 증진시키기 위하여 CVD법에 의한 SiC 코팅과 PCS 함침법을 응용하여 실험을 행하였다. 전자현미경으로 시편의 미세구조를 관찰 한 결과 CVD법에 의해서는 표면에 SiC가 고르게 증착되었으며, 함침법에 의해서는 각 탄소 섬유의 표면에 PCS가 wetting된 후 SiC로의 전이가 잘 일어났음을 확인하였고, 이로 인하여 각 섬유들의 결합력을 증대시키고 기계적물성에 증진을 가져왔음을 확인하였다. PCS 함침된 탄소/탄소 복합체 시편은 함침되지 않은 시편에 비해 밀도는 25 %, 곡강도 값은 3.5배, 내산화성은 2.8배가 증가하는 현격한 기계적 물성이 증가함을 보였다. 이러한 증가는 CVD법에 의해 코팅된 탄소/탄소 복합체 사편보다도 우수한 기계적 성질을 나타내였다.