Abstract
The current ASTM C227-90 is a prescription on the mortar-bar method. This recornrnends that mortar-bars should be made using a mixing ratio by weight of 675 grams aggregate to 300 grams cement, and their initial lengths should be measured in $24{\pm}2$ hours. This method emphasizes that the prepare sample mortar-bars and calculate expansion rates of them. This method requires constant G values (effective gauge lengths) of denominator in the calculation formula, which are fixed either at 10 inches or 250mm. This study, based on experimental approaches, reexamines the suggestions made by those two prescriptions above and important results are summarized in the following. 1. Not only alkali-aggregate reaction but also interaction of interstitial and gel water are responsible for expansion of mortar-bars. This requires partial modification of the current ASTM C227-90. 2. A mixing ratio by volume rather than by weight of aggregate to cement is recommendable for measuring the amount of expansion resulting from alkali-aggregate reaction and from interstitial water. 3. The method of when to measure initial lengths and how to calculate expansion rate suggested by ASThI C227-90 and Cl90-93a should partly be modified for more accurate results.
현행 ASTM C227-90은 모르타봉 시험법에 대한 규정인데 동 규정에 의하면 시험용 모르타르봉으 제작에 골재와 시멘트를 각각 675g과 300g을 쓰도록 무게비로 제시하고 있으며 제작된 모르타르봉의 초기길이 측정시기는 $24{\pm}2$시간으로 규정되어 있다. 또한 모르타르봉의 팽창원인을 알카리-골재반응에 두고 있다. ASTM C490-93a는 모르타르봉의 제작방법과 팽창률 계산방법이 소개되어 있는데 규정에 의하면 계산공식으 분모 G값을 10" 혹은 250mm로 고정시키고 있다. 본 연구는 위에 소개한 내용에 대한 실험적 연구를 통하여 다음과 같은 결론에 도달하였다. 첫째, 모르타르봉의 팽창은 알카리-골재반응만에 의한 것이 아니고 그 외 간극수와 겔수의 복합적인 작용에 의한 것이므로 ASTM C227-90의 내용을 일부 수정할 필요가 있다. 둘째, 골재에 의한 모르타르봉의 팽창원인 즉 알카리-골재반응과 간극수에 의한 팽창량을 알기 위하여는 골재와 시멘트의 배합비를 무레비 대신에 부피비로 제시함이 바람직 하다. 세째, ASTM C227-90과 ASTM C490-93a에서 제시한 모르타르봉의 초기길이 측정시기와 팽창률 계산방법은 더욱 정밀한 계산결과를 얻기 위하여 부분적인 수정이 필요하다.