BaMgF$_{4}$ 를 이용한 금속-강유전체박막-실리콘(MFS) 구조의 특성

Properties of metal-ferroelectric thin film-silicon(MFS) structure using BaMgF$_{4}$

  • 김광호 (청주대학교 반도체공학과) ;
  • 김제덕 (청주대학교 반도체공학과) ;
  • 유병곤 (한국전자통신연구소 반도체연구단)
  • 발행 : 1996.05.01

초록

Use of a rapid thermal annealing (RTA) technique is shown to improve the properties of metal-ferroelectric BaMgF$_{4}$-silicon structures. The fluoride film was deposited in an ultra-high vacuum system at asubstrate temperature of 300$^{\circ}C$. A post-deposition annelaing was conducted for 10 seconds at 600.deg. C in a vacuum of 0.1 Torr, using a home-made RTA apparatus. The results showed that the resistivity of the ferroelectric BaMgF$_{4}$ film from a typical value of 1-2${\times}10^{11}{\Omega}{\cdot}cm$ before the annealing to about 5${\times}10^{13}{\Omega}{\cdot}cm$ and reduce the interface state density of the BaMgF$_{4}$/Si interface to about 8${\times}10^{10}cm^{2}{\cdot}$eV. Ferroelectric hysteresis measurements using a sawyer-tower circuit yielded remanent polarization and coercive field values of about 0.5$\mu$C/cm$^{2}$ and 80 kV/cm, respectively. the typical remanent polarization of the BaMgF$_{4}$ films ont he (100) and (111) oreientated silicon wafers were 0.5 - 0.6 $\mu$C/cm$^{2}$ and that of th efilms on the (110) wafers was 1.2$^{\circ}C$/cm$^{2}$.

키워드