A STUDY ON THE FRACTURE STRENGTH OF ALL-CERAMIC CROWNS

수종 전부도재관의 파절강도에 관한 비교연구

The pupose of this study was to compare the fracture strength of five kinds of all-ceramic crowns(Vintage, Dicor Empress-staining, Empress-layering, In-Ceram) luted with glass ionomer cerment and composite resin cement and to evaluate the effect of cements on the fracture stregth of all ceramic crowns. Five groups of twelve uniform sized all-ceramic crown specimens were fabricated. Six specimens of each group were cemented with glass ionomer cement(Fuji G.I. Cement) and the remaining six specimens of each group were etched, silane-treated, and cemented with composite resin cement(Bistite resin cement). The crowns were stored in water$(37^{\circ}C)$ for 1 day prior to loading in an Instron, using a steel ball(diameter 4mm) at a crosshead speed of 0.5mm/min. The crowns were angled $30^{\circ}$, so the steel ball contacted with the crowns 2mm lingual from the mid-incisal edge. The results obtained were summarized as follows ; 1. With G.I. cement, mean fracture load(Kg) Were : Intage : $18.33{\pm}1.47$ ; Empress-staining : $23.92{\pm}6.67$ ; Dicor : $24.0{\pm}5.81$ ; Empress-layering : $26.92{\pm}2.80$ ; In-Ceram : $51.58{\pm}6.87$ ; ANOVA revealed a significant difference existed(p<0.05) between the group A(Vintage, Dicor, Empress-staining, Empress-layering) and group B(In-Ceram). 2. With Resin cement, mean fracture load(Kg) were : Intage : $22.75{\pm}4.97$ ; Dicor : $42.75{\pm}7.07$ ; Empress-staining : $44.08{\pm}7.99$ ; Empresslayering : $50.42{\pm}5.43$ ; In-Ceram : $52.58{\pm}6.51$ ; ANOVA revealed a significatnt difference existed(p<0.05) between the group A(Vintage) and B(Dicor, Empress-staining Empress-alyering, In-Ceram). 3. Resin cement significantly increased the fracture strength of the all-ceramic crowns for Dicor(156%), Empress-staining(185%), Empress-alyering(187%)(p<0.05); but did not increase the fracture strength of Vintage(128%) and In-Ceram(101%)(p>0.05). 4. Majority of the all-ceramic crowns show a wedge fracture extending through proximal surfaces to an apex, usually apical third(with G.I. cement) or middle third(with Resin cement) of the facial surface.