Abstract
This study was conducted to the effect of temporary cement on the adhesiveness of dentin bonding agent to dentin surface. One hundred freshly extracted bovine mandibular incisors were grinded to expose flat labial dentin surface. The dentin surfaces were temporarized with either eugenol-containing temporary cement(TemBond and Zinc Oxide Eugenol cement) or non-eugenol temporary cement(Nogenol and TempBond NE) for 7days, and then the temporarization was removed with surgical currette and the exposed dentin surfaces were water-rinsed. Bonding specimens were made by use of All-Bond 2 and Super-Bond C&B dentin bonding agent, and stored in $37^{\circ}C$ distilled water for 24hours. The tensile bond strenth and the cohesive failure rate were measured, and then the pretreated dentin surfaces which the temporary cement had been applied to and removed from and the fractured dentin surfaces after bonding test were examined under scanning electron microscope. The results were as follows : In case of bonding with All-Bond 2, tensile bond strength of each experimental group was lower than that of the control group(p<0.05), but there was no significant difference between the bond strengths of the control group and each experimental group in case of bonding with Super-Bond C&B(p>0.05). No significant difference between tensile bond strength of experimental group, whether temporary cement contains eugenol or not, was seen(p>0.05). In case of bonding with All-Bond 2, the control group showed cohesive-adhesive mixed failure mode and the experimental groups mainly showed adhesive failure mode, but in case of bonding with Super-Bond C&B, almost of the control and the experimental groups mainly showed cohesive failure mode. On SEM examination, all of the dentin specimens pretreated with either 10 % phosphoric acid or 10% citric acid after application of the temporary cements demonstrated remnants of temporary cement attached to dentin surface.
Temporary cement가 상아질 접착제의 접착 성능에 미치는 영향을 평가하기 위해 소의 하악 전치 100개를 사용하여 순면의 상아질을 노출 시키고 유지놀을 함유하지 않은 Nogenol 및 TempBond NE와 유지놀을 함유한 TempBond 및 산화아연 유지놀세멘트를 각각 도포하여 7일 경과 후 제거하였다. All-Bond 2 및 SuperBond C&B 상아질 접착제를 제조회사의 지시대로 사용하여 접착시킨뒤 $37^{\circ}C$ 항온조에서 24시간 보관 후 인장접착강도를 측정하고, 응집 파단율을 산정하였다. 그리고 temporary cement를 적용하지 않은 상아질면과 temporary cement를 도포하였다가 제거한 상아질면에 10% 인산 수용액 및 10% 구연산 수용액으로 각각 산처리한 상아질 표면성상과 접착실험후의 파단면을 주사전자현미경으로 관찰하여 다음의 결과를 얻었다. 1. All-Bond 2로 접착시킨 경우에 는 사용한 temporary cement의 종류에 관계없이 실험군의 인장접착강도가 temporary cement를 사용하지 않은 대조군에 비해 유의하게 낮게 나타냈으나(p<0.05), Super-Bond C&B로 접착시킨 경우에는 유의한 차이가 없었다.(p>0.05). 2. 유지놀을 함유하는 temporary cement와 유지놀을 함유하지 않는 temporary cement를 각각 적용한 실험군들의 인장접착 강도 간에는 유의한 차이가 없었다.(P>O.05). 3. 응집파단율 산정결과 All-Bond 2로 접착 시킨 경우에는 대조군에서 응집-부착성의 혼합파단양상이，실험군에서는 부착성 파단양상이 주로 나타났으나, Super-Bond C&B로 접착 시킨 경우에는 대조군과 실험군 모두에서 용접성파단양상이 우세하게 나타났다. 4. 주사전자현미경적 관찰상에서 temporary cement의 종류에 관계없이 temporary cement를 도포한후 제거하고 10% 인산 수용액 또는 10-3 용액으로 전처리한 모든 시편에서 미세한 temporary cement의 잔존물을 관찰할 수 있었다.