The Behavior of Carbon on the Damping Characteristics of Fe-5.7% Al Alloy

Fe-5.7% Al 합금의 제진특성에 미치는 탄소의 거동

Carbon and small amounts of alloying elements were added in Fe-5.7% Al ferromagnetic damping alloy. The specific damping capacities(SDC) of these alloys were investigated in relation to the grain size and the magnetic hysteresis loops. The behavior of carbon was analysed by XRD and EDS. These alloys showed characteristic damping nature of ferromagnetic damping materials. The alloying elements decreased SDC and especially the carbon was remarkable. The SDC was observed to be not related with the grain size but with the magnetic hysteresis loop area. The remarkable decrease of SDC by carbon addition was attributed to the locking migration of $90^{\circ}$ magnetic domain wall by the interstitial carbon in Fe-Al solid solution. However, the carbides also seems to decrease the SDC.

Fe-5.7% Al 합금에 탄소 및 미량 합금원소를 첨가하고 그 제진특성 변화를 결정립 크기 및 자기적 특성과 관련하여 관찰하였으며, 탄소의 거동을 XRD 및 EDS로 조사하였다. 이 합금은 강자성형 제진 양상을 나타냈고, 제3원소 첨가는 그 SDC를 악화시키며 특히 탄소는 현저하였다. 제진 특성은 결정립 크기와는 직접적인 상관관계가 없었고, 자기이력곡선 면적은 상관관계가 있었다. 탄소가 이 합금의 제진특성을 악화시키는 원인은 고용탄소에 의한 $90^{\circ}$ 자구벽의 고착이 주원인이었으며, 탄화물도 자구벽의 이동을 방해할 것이므로 제진특성에 악영향을 미치는 것으로 해석되었다.