Permeability Properties of High Fly Ash Concrete

높은 혼합비율의 플라이 애쉬를 갖는 콘크리트의 침투성 특징에 관한 연구

The permeability of concrete is closely related to the durability and the latter may be expressed by measuring permeability of concrete. According to the results, the permeability of fly ash concrete was lower than that of OPC(PC1) concrete and decreased with increasing fly ash levels(l5%, 30% and 45%). The permeability values of concrete cured in water is significantly lower than those of concrete cured in air, but the differences were reduced with increasing fly ash level. In comparison with OPC(PC1) concrete and high fly ash concrete containing enhanced early strength cements, the latter also had a lower permeability than the former. The permeability of concrete cured in water was decreased with curing time(28 and 180 days) irrespectwe of cement types. However, the trend of results cured in air was opposite to that cured in water due to the rnicrocrackinp: of concrete. It was found that the properties of strength and permeability of concrete were related each other. However, the permeability of concrete was more dependant upon the type of binder used in concrete.

콘크리트의 침투성은 내구성과 밀접한 관계가 있고, 콘크리트의 내구성은 침투성 특성에 의해서 간접적으로 측정될 수 잇다. 실험 결과에 의하면 콘크리트의 침투성에서 플라이애쉬의 양이 증가할수록 (15%, 30%, 그리고45%) 침투성이 낮아졌으며, 기건양생한 콘크리트가 수중양생한 것에 비해서 월등히 높은 침투성을 보여 주었으나. 그 차이점은 플라이애쉬를 섞는 양이 많을수록 줄어 들었다. 높은 비율의 플라이애쉬(45%) 다양한 조강 시멘트를 섞어 만든 콘크리트에서도, 플라이애쉬 콘크리트가 보통(PCI)콘크리트보다 낮은 침투성을 보여주었다. 콘크리트는 양생기간이 길어짐에 따라 시멘트종류에 관계없이 침투성이 낮아졌으나, 기건양생시에는 증가하는 것을 보여주었다. 침투성 특징에서 모든 콘크리트는 물을 이용해 시험한 것이 기체를 이용해 시험한 것 보다 항상 낮은 값을 갖는다는 것이 발견되었다. 콘크리트의 침투성은 그것의 강도가 증가함으로써 줄어드는 것을 발견하였으나, 침투성의 특징은 주로 사용한 시멘트종류와 좀더 밀접한 관계가 있는 것으로 나타났다.