The structure analysis of $Y_1Ba_2Cu_3O_x$ high Tc superconductor based on rietveld method

리트벨트 해석법을 이용한 $Y_1Ba_2Cu_3O_x$ 고온 초전도체의 구조분석

For the execution of RIETAN program adopting Rietveld Analysis Method, the sample superconductor is made according to the solid state synthesis method at 920.deg. C for 24hrs, and was examined for the optimization of parameters needed to analyze Rietveld method with the input of the measured pattern data after measuring the pattern resulted from the X-ray diffraction. It was proven that the lattice constant of the superconductor which was consisted of Pmmm orthorhombic crystal structure in the analyzed space group correspond to the presented theoretical lattice constant a=3.8887(8).angs., b=3.8238(4).angs., c=11.7079.angs.. Therefore, it was examined and confin-ned that the R factor, which was compensated after analyzing the structure of superconductor resulted from this experimented data with the computer simulation, was refined to $R_{wp}$=8.83[%], $R_{P}$=6.47[%], $R_{I}$=10.08[%], $R_{F}$=7.19[%], $R_{E}$=3.76[%]. On the basis of these experimental data, the significant parameter such as the scale factor(S) and the zero point shift(Z) and FWHM value(U,V,W) were optimized as follows; S=2.0827E-3, Z=0.2146, U=4.2761E-2, V=1.7983E-2, and W=2.6768E-2.2.2.2.2.2.