The characterization for the Ti-silicide of $N^+P$ junction by 2 step RTD

2단계 RTD방법에 의한 $N^+P$ 접합 티타늄 실리사이드 특성연구

Two step RTD(Rapid Thermal Diffussion) of P into silicon wafer using tungsten halogen lamp was used to fabricated very shallow n$^{+}$p junction. 1st RTD was performed in the temperature range of 800.deg. C for 60 see and the heating rate was in the 50.deg. C/sec. Phosphrous solid source was transfered on the silicon surface. 2nd RTD process was performed in the temperature range 1050.deg. C, 10sec. Using 2 step RTD we can obtain a shallow junction 0.13.mu.m in depth. After RTD, the Ti-silicide process was performed by the two step RTA(Rapid Thermal Annealing) to reduced the electric resistance and to improve the n$^{+}$p junction diode. The titanium thickness was 300.angs.. The condition of lst RTA process was 600.deg. C of 30sec and that of 2nd RTA process was varied in the range 700.deg. C, 750.deg. C, 800.deg. C for 10sec-60sec. After 2 step RTA, sheet resistance was 46.ohm../[]. Ti-silicide n+p junction diode was fabricated and I-V characteristics were measured.red.