Abstract
This study was carried out to remove the iron and impurities usmg hydrocyclone and HGMS for recycling of sludge from the granite stone cutting and polishing industrγ in the basic of chemi떠1 analysis and minerallogical investigation. This sludge consist of 70.9% $SiO_2$ 13.6% $Al_2O_3$ and It also contained 2.52% of $Fe_2O_7$ and 0.29% of $TiO_2$, as a main impurities to decrease the whiteness. As the result of hydrocyclone experiment, It was very good condition that are 100~150 g/l of sludge amount, 2.0~ 2.5 mm of underflow nozzle size, and 1.2~1.6 kg/$\textrm{cm}^2$ of pressure for 85% sludge product with the $-37{\mu}\textrm{m}$ size. $Fe_2O_3$ and $TiO_2$, contents by treatment of HGMS were decreased with 0.65% and 0.07% each at 10,000 gauss of magnetic field strength, and addih$\upsilon$n of Sodium tripolyphosphate as a dispersant was effected to get low grade F Fe,Ol and TiO, concentrate. PhYSIcal properties of this stone sludge product were showed 58.5% of whiteness, 1 13.4% of firing shrinkage and 3.0812 $\textrm{m}^2$/g of specific surface area.
화강암 석재가공 공장의 절단 및 연마공정시 발생하는 슬러지를 재활용하기 위해 광물학적 조사 및 화학분석을 실시하였으며, 철분 및 불순물등의 제거 실험을 위한 습식 하드로싸이클론 및 고구배자력선별 실험을 실시하였다. $SiO_2$와 $Al_2O_3$의 함량은 각각 70.9%, 13.6%이었으며, 요업 및 사업원료로 사용하는데 있어서 백색도를 저하시키는 불순물인 $Fe_2O_3$함량은 2.52%로 비교적 많았으며, $TiO_2$함량은 0.29%이였다. 하이드로싸이클론 실험결과 슬러지의 양은 100~150g/l, Underflow Nozzle의 크기는 2.0~2.5mm, 압력은 1.2~1.6kg/$\textrm{cm}^3$의 조건에서 $-37{\mu}\textrm{m}$ 입도 85%를 얻을 수 있었다. 고구배자력실험결과 10,000가우스에서 $Fe_2O_3$는 0.65%, $TiO_2$는 0.07%인 비자착산물을 얻을 수 있었으며, 분산제로 Sodium tripolyphosphate를 사용한 결과 탈철에 효과적이였다. 슬러지 산물의 물리적인 특성은 백색도 68.5%, 수축율 13.4%, 비표면적 $3.0812m^2/g$로 나타났다.