Effects of NiFeCo of NiFe Insertion Layers on the Giant Magnetoresistance Behavior of Ni/Cu Artificial Superlattice

Ni/Cu 인공초격자에서 NiFeCo 및 NiFe 계면 삽입층이 거대자기저항 거동에 미치는 영향

Ultra thin layers of NiFeCo or NiFe were inserted at the interfaces of Ni and Cu to form a multilayer structure. In case of inserting a NiFe layer, the magnetoresistance was about 6%, the saturation magnetic field was 50 Oe and the hysteresis of R-H (resistance-magnetic field) was very small. In case of inserting a NiFeCo layer, the magnetoresistance increased to about 7% but the saturation magnetic field and hysteresis were also increased. The increase of the output under biased magnetic field was much larger in case of inserting a NiFe layer because of relatively smaller hysteresis in R-H behavior.

Ni/Cu 인공초격자의 계면에 얇은 NiFeCo와 NiFe층을 삽입시 Ni/Cu 인공초격자의 자기 저항 거동에 미치는 영향에 관해 연구하였다. NiFe층이 Ni/Cu 인공초격자의 계면에 삽입된 경우 6%의 자기저항과 50 Oe의 포화자장을 보였으며 이때의 자기저항곡선은 hysteresis를 거의 보이지 않았다. NiFeCo층이 삽입된 경우는 자기저항값은 7%를 보였으나 포화자장과 hysteresis가 많이 증가하였다. 교류자장원을 이용한 동적자기저항을 측정한 결과 bias 자장하에서 자기저항의 증가폭이 NiFe층을 삽입한 경우가 NiFeCo를 삽입한 경우보다 컸으며 이는 hysteresis가 작았기 때문으로 해석된다.