Abstract
The crystallographic and magnetic properties of the ferrimagnetic $Ni_{0.5}Co_{0.5}Fe_{2}O_{4}$ have been studied by X-ray and $M\"{o}ssbauer$ measurements. The Crystal structure is found to be spinel structure with the lattice constant $a_{0}=8.346{\pm}0.005\;{\AA}$. $M\"{o}ssbauer$ spectra of $Ni_{0.5}Co_{0.5}Fe_{2}O_{4}$ have been taken at various temperatures rallging from 13 to 780 K. The isomer shifts indicate that the valence states of the Fe ions for tetrahedral(A) and octahedral(B) sites have ferric character. Debye temperatures for the A and B sites are found to be $441{\pm}5\;K$ and $321{\pm}5\;K$, respectively. Atomic migration from the A to the B sites starts near 500 K and increases rapidly with increasing temperature to such a degree that 51 % of the ferric ions at the A sites have moved over to the B sites by 700 K.
준강자성 $Ni_{0.5}Co_{0.5}Fe_{2}O_{4}$의 결정학적 및 자기적 성질을 X-선 회절법과 $M\"{o}ssbauer$ 분광법으로 연구하였다. 결정구조는 입방 스피넬 구조를 갖으며, 격자상수 $a_{0}=8.346{\pm}0.005\;{\AA}$임을 알았다. $M\"{o}ssbauer$ spectrum 은 13 K 부터 780 K 영역까지 취하였다. 상온에서 이성질체이동 결과 사면체(A), 팔면체(B)자리 모두 철 이온의 전하상태가 +3가 임을 알았다. 결정내의 Debye 온도가 A자리는 $441{\pm}5\;K$이며 B 자리는 $321{\pm}5\;K$로 결정하였다. 또한 $Fe^{3+}$ 이온이 A자리에서 B자리로의 원자이동은 500 K 근처에서 시작되었으며, 온도 증가에 따라 급격히 증가하여 700 K 에서 Fe 이온의 이동률은 51%이었다.